Taita Chemical 1000D

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

TAITALAC 1000D ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Telephone housing / House-ware, Office Automation, Electrical appliances.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Housewares

Automotive & Transportation — Automotive

Exterior & Body

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Processing Methods: Injection Molding
Color: White
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Flame Rating: UL 94 HB
Technology: Plastics
Characteristic: Injection
Medium high impact
Good flow for process
Gloss
Material Features: Good Flow
High Impact Performance
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
Plastics and Elastomers End Uses: Appliances
Housewares
Office Automation Equipment
Television Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

3 rows

Characteristic	Value	Unit	Method
Moisture Absorption Equilibrium (23°C/50% RH)	max. 0.3	wt%	ASTMD570
Mold Shrinkage (60×60×2mm SFlow)	max. 0.4	wt%	ASTMD955
Rockwell Hardness (23°C, R-scale)	110.0	R-scale	ASTMD785

Table 2 of 7

7 rows

Characteristic	Value	Unit	Method
Elongation at Break (23°C, 5 mm/min)	30.0	%	ASTMD638
Flexural Modulus (23°C, 2.8 mm/min)	25000.0	kg/cm2	ASTMD790
Flexural Yield (23°C, 2.8 mm/min)	720.0	kg/cm2	ASTMD790
Izod Impact Strength (23°C, 1/4” Notched)	22.0	kg-cm/cm	ASTMD256
Izod Impact Strength (23°C, 1/8” Notched)	25.0	kg-cm/cm	ASTMD256
Tensile Strength at Break (23°C, 5 mm/min)	380.0	kg/cm2	ASTMD638
Tensile Strength at Yield (23°C, 5 mm/min)	430.0	kg/cm2	ASTMD638

Table 3 of 7

8 rows

Characteristic	Value	Unit	Method
Heat Distortion Temperature (Unannealing 1.8MPa)	86.0	°C	ASTMD648
RTI Elec (1.5 mm)	60.0	—	UL 746
RTI Elec (3.0 mm)	60.0	—	UL 746
RTI Imp (1.5 mm)	60.0	—	UL 746
RTI Imp (3.0 mm)	60.0	—	UL 746
RTI Str (1.5 mm)	60.0	—	UL 746
RTI Str (3.0 mm)	60.0	—	UL 746
Vicat Softening Temperature (50°C/hr , 1 kg load)	103.0	°C	ASTMD1525

Table 4 of 7

11 rows

Characteristic	Value	Unit	Method
Arc Resistance	PLC 7	—	ASTM D495
Arc Tracking Rate (0.062 inch above)	0.0	in/min	UL-746A
Comparative Tracking Index	PLC 1	—	UL 746
High Amp Arc lgnition (1.5 mm)	PLC 0	—	UL 746
High Amp Arc lgnition (3.0 mm)	PLC 0	—	UL 746
High Current Arc Ignition (0.062 inch above)	200.0	Arcs	UL-746A
High Voltage Arc Tracking Rate	PLC 0	—	UL 746
Hot Wire Ignition (0.062 inch above)	17.0	Secs	UL-746A
Hot-Wire Ignition (1.5 mm)	PLC 3	—	UL 746
Hot-Wire Ignition (3.0 mm)	PLC 3	—	UL 746
Relative Temperature Index (0.062 inch above)	60.0	°C	UL-746B

Table 5 of 7

4 rows

Characteristic	Value	Method
Flame Rating (1.5 mm, ALL)	HB	UL 94
Flame Rating (1.5 mm, ALL)	HB 75	IEC 60695-11-10,-20
Flame Rating (3.0 mm, ALL)	HB 40	IEC 60695-11-10,-20
Flame Rating (3.0 mm, ALL)	HB	UL 95

Table 6 of 7

12 rows

Characteristic	Value	Unit
Back Pressure	50 - 70	psi(Mpa)
Drying Temperature	80 - 85	°C
Drying Time	2.0 - 4.0	hr
Front Zone	190 - 220	°C
Injection Pressure	Moderate to Moderately High	—
Injection Speed	Moderate to Fast	—
Melt Zone	180 - 190	°C
Middle Zone	200 - 230	°C
Mold Temperature	40 - 70	°C
Nozzle	210 - 240	°C
Rear Zone	190 - 220	°C
Screw Speed	30 - 100	rpm

Table 7 of 7