Taita Chemical 3000D

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

TAITALAC 3000D ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Luggage, Extruded plate, Tool box, Low temperature use, Vacuum molding applications.

Properties

Physical Form: Pellets
Solid

Product families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Processing Methods: Blow Molding, Extrusion, Thermoforming
Color: White
Markets: Consumer Goods
Applications: Consumer Goods — Housewares
Consumer Goods — Luggage & Leather Goods
Flame Rating: UL 94 HB
Technology: Plastics
Characteristic: High impact
Extrusion
Good chemical resistance
Material Features: Good Toughness
High Impact Resistance
High Melting Point
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
Plastics and Elastomers End Uses: Housewares
Luggage
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Blow Molding
Extrusion
Thermoforming

Technical data

Table 1 of 7

7 rows

Characteristic	Value	Unit	Method
Elongation at Break (23°C, 5 mm/min)	40.0	%	ASTMD638
Flexural Modulus (23°C, 2.8 mm/min)	21000.0	kg/cm2	ASTMD790
Flexural Yield (23°C, 2.8 mm/min)	600.0	kg/cm2	ASTMD790
Izod Impact Strength (23°C, 1/4” Notched)	40.0	kg-cm/cm	ASTMD256
Izod Impact Strength (23°C, 1/8” Notched)	45.0	kg-cm/cm	ASTMD256
Tensile Strength at Break (23°C, 5 mm/min)	360.0	kg/cm2	ASTMD638
Tensile Strength at Yield (23°C, 5 mm/min)	390.0	kg/cm2	ASTMD638

Table 2 of 7

3 rows

Characteristic	Value	Unit	Method
Moisture Absorption Equilibrium (23°C/50% RH)	max. 0.3	wt%	ASTMD570
Mold Shrinkage (60×60×2mm SFlow)	max. 0.4	wt%	ASTMD955
Rockwell Hardness (23°C, R-scale)	102.0	R-scale	ASTMD785

Table 3 of 7

5 rows

Characteristic	Value	Unit	Method
Heat Distortion Temperature (Unannealing 1.8MPa)	86.0	°C	ASTMD648
RTI Elec (1.5 mm)	60.0	—	UL 746
RTI Imp (1.5 mm)	60.0	—	UL 746
RTI Str (1.5 mm)	60.0	—	UL 746
Vicat Softening Temperature (50°C/hr , 1 kg load)	101.0	°C	ASTMD1525

Table 4 of 7

7 rows

Characteristic	Value	Unit	Method
Arc Resistance	PLC 6	—	ASTM D495
Comparative Tracking Index	PLC 1	—	UL 746
Dielictric Strength	22.0	KV/mm	ASTM D149
High Amp Arc lgnition (1.5 mm)	PLC 0	—	UL 746
High Voltage Arc Tracking Rate	PLC 0	—	UL 746
Hot-Wire Ignition (1.5 mm)	PLC 3	—	UL 746
Volume Resistivity	1.0E+16	Ohm-cm	ASTM D257

Table 5 of 7

2 rows

Characteristic	Value	Method
Flame Rating (1.5 mm)	HB	UL 94
Flame Rating (1.5 mm)	HB 75	IEC 60695-11-10,-20

Table 6 of 7

12 rows

Characteristic	Value	Unit
Back Pressure	50 - 70	psi(Mpa)
Drying Temperature	80 - 85	°C
Drying Time	2.0 - 4.0	hr
Front Zone	205 - 235	°C
Injection Pressure	Low to Moderate	—
Injection Speed	Low to Moderate	—
Melt Zone	190 - 200	°C
Middle Zone	215 - 245	°C
Mold Temperature	40 - 70	°C
Nozzle	225 - 245	°C
Rear Zone	205 -235	°C
Screw Speed	30 - 100	rpm

Table 7 of 7