Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

TAITALAC 3100R ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Automobile parts, Motorcycle parts, Shoe Heel, Profile Extrusion and Low temperature use applications.

Properties

Physical Form: Pellets
Solid

Product families

Applications

Consumer Goods — Other Consumer Goods Applications

Automotive & Transportation — Automotive

Aftermarket Parts & Components

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Processing Methods: Extrusion
Color: White
Markets: Automotive & Transportation
Consumer Goods
Flame Rating: UL 94 HB
Technology: Plastics
Characteristic: Super high impact strength and rigidity
Extrusion/Injection
Material Features: Creep Resistant
Good Toughness
High Melting Point
High Rigidity
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
Plastics and Elastomers End Uses: Safety Helmets
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion

Technical data

Table 1 of 5

3 rows

Characteristic	Value	Unit	Method
Moisture Absorption Equilibrium (23°C/50% RH)	max. 0.3	wt%	ASTMD570
Mold Shrinkage (60×60×2mm SFlow)	max. 0.4	wt%	ASTMD955
Rockwell Hardness (23°C, R-scale)	100.0	R-scale	ASTMD785

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Elongation at Break (23°C, 5 mm/min)	30.0	%	ASTMD638
Flexural Modulus (23°C, 2.8 mm/min)	22000.0	kg/cm2	ASTMD790
Flexural Yield (23°C, 2.8 mm/min)	620.0	kg/cm2	ASTMD790
Izod Impact Strength (23°C, 1/4” Notched)	43.0	kg-cm/cm	ASTMD256
Izod Impact Strength (23°C, 1/8” Notched)	48.0	kg-cm/cm	ASTMD256
Tensile Strength at Break (23°C, 5 mm/min)	370.0	kg/cm2	ASTMD638
Tensile Strength at Yield (23°C, 5 mm/min)	420.0	kg/cm2	ASTMD638

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Distortion Temperature (Unannealing 1.8MPa)	87.0	°C	ASTMD648
Vicat Softening Temperature (50°C/hr , 1 kg load)	103.0	°C	ASTMD1525

Table 4 of 5

12 rows

Characteristic	Value	Unit
Back Pressure	50 - 70	psi(Mpa)
Drying Temperature	80 - 85	°C
Drying Time	2.0 - 4.0	hr
Front Zone	200 - 230	°C
Injection Pressure	Moderately High to high	—
Injection Speed	Moderate to Fast	—
Melt Zone	185 - 195	°C
Middle Zone	210 - 240	°C
Mold Temperature	40 - 70	°C
Nozzle	220 - 240	°C
Rear Zone	200 - 230	°C
Screw Speed	30 - 100	rpm

Table 5 of 5