To catalogue
Taita Chemical 8540T
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
TAITALAC 8540T ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Business machine, Computer, Complex shaped product and Battery.
Properties
- Physical Form
- Pellets
- Solid
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Characteristic
- Medium high impact
- Injection molding
- High flow for process
- UL 1/16" V-0
- Material Features
- Flame Retardant
- High Flow
- High Impact Performance
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
- Plastics and Elastomers End Uses
- Appliances
- Battery Cases
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption Equilibrium (23°C/50% RH) | max. 0.3 | wt% | ASTMD570 |
| Mold Shrinkage (60×60×2mm SFlow) | max. 0.4 | wt% | ASTMD955 |
| Rockwell Hardness (23°C, R-scale) | 102.0 | R-scale | ASTMD785 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (23°C, 5 mm/min) | 20.0 | % | ASTMD638 |
| Flexural Modulus (23°C, 2.8 mm/min) | 22000.0 | kg/cm2 | ASTMD790 |
| Flexural Yield (23°C, 2.8 mm/min) | 600.0 | kg/cm2 | ASTMD790 |
| Izod Impact Strength (23°C, 1/4” Notched) | 17.0 | kg-cm/cm | ASTMD256 |
| Izod Impact Strength (23°C, 1/8” Notched) | 20.0 | kg-cm/cm | ASTMD256 |
| Tensile Strength at Break (23°C, 5 mm/min) | 300.0 | kg/cm2 | ASTMD638 |
| Tensile Strength at Yield (23°C, 5 mm/min) | 380.0 | kg/cm2 | ASTMD638 |
Table 3 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Unannealing 1.8MPa) | 77.0 | °C | ASTMD648 |
| RTI Elec (1.5 mm) | 60.0 | — | UL 746 |
| RTI Elec (3.0 mm) | 60.0 | — | UL 746 |
| RTI Elec (6.0 mm) | 60.0 | — | UL 746 |
| RTI Imp (1.5 mm) | 60.0 | — | UL 746 |
| RTI Imp (3.0 mm) | 60.0 | — | UL 746 |
| RTI Imp (6.0 mm) | 60.0 | — | UL 746 |
| RTI Str (1.5 mm) | 60.0 | — | UL 746 |
| RTI Str (3.0 mm) | 60.0 | — | UL 746 |
| RTI Str (6.0 mm) | 60.0 | — | UL 746 |
| Vicat Softening Temperature (50°C/hr , 1 kg load) | 94.0 | °C | ASTMD1525 |
Table 4 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Arc Resistance | PLC 7 | — | ASTM D495 |
| Arc Tracking Rate (0.062 inch above) | 4.2 | in/min | UL-746A |
| Comparative Tracking Index | PLC 2 | — | UL 746 |
| Dielictric Strength | 22.0 | KV/mm | ASTM D149 |
| High Amp Arc lgnition (1.5 mm) | PLC 4 | — | UL 746 |
| High Amp Arc lgnition (3.0 mm) | PLC 4 | — | UL 746 |
| High Current Arc Ignition (0.062 inch above) | 10.0 | Arcs | UL-746A |
| High Voltage Arc Tracking Rate | PLC 0 | — | UL 746 |
| Hot Wire Ignition (0.062 inch above) | 57.0 | Secs | UL-746A |
| Hot-Wire Ignition (1.5 mm) | PLC 2 | — | UL 746 |
| Hot-Wire Ignition (3.0 mm) | PLC 1 | — | UL 746 |
| Relative Temperature Index (0.062 inch above) | 60.0 | °C | UL-746B |
Table 5 of 7
3 rows| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.5 mm) | V-0 | UL 94 |
| Flame Rating (3.0 mm) | V-0, 5VA | IEC 60695-11-10,-20 |
| Flame Rating (6.0 mm) | V-0 5VA | IEC 60695-11-10,-21 |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 50 - 70 | psi(Mpa) |
| Drying Temperature | 70 - 75 | °C |
| Drying Time | 2.0 - 4.0 | hr |
| Front Zone | 170 - 200 | °C |
| Injection Pressure | Moderate to Moderately high | — |
| Injection Speed | Moderate to Fast | — |
| Melt Zone | 165 - 175 | °C |
| Middle Zone | 180 - 210 | °C |
| Mold Temperature | 40 - 70 | °C |
| Nozzle | 190 - 220 | °C |
| Rear Zone | 170 - 200 | °C |
| Screw Speed | 30 - 100 | rpm |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Rate (200°C, 5kg load) | 5.0 | g/10min | ASTM D1238 |
| Melt Volume Rate (220°C, 10kg load) | 45.0 | g/10min | ASTM D1238 |
| Specific Gravity (23°C) | 1.17 | g/cm3 | ASTM D792 |