To catalogue
Taita Chemical 3000P
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
TAITALAC 3000P ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Automobile parts, Motorcycle parts, Helmets and Low temperature use.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Other Consumer Goods Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Extrusion
- Color
- White
- Markets
- Automotive & Transportation
- Consumer Goods
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Characteristic
- Super high impact strength and rigidity
- Extrusion/Injection
- Low temperature high impact resistant
- Material Features
- Low Temperature Impact Resistance
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
- Plastics and Elastomers End Uses
- Safety Helmets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (23°C, 5 mm/min) | 40.0 | % | ASTMD638 |
| Flexural Modulus (23°C, 2.8 mm/min) | 21000.0 | kg/cm2 | ASTMD790 |
| Flexural Yield (23°C, 2.8 mm/min) | 600.0 | kg/cm2 | ASTMD790 |
| Izod Impact Strength (23°C, 1/4” Notched) | 40.0 | kg-cm/cm | ASTMD256 |
| Izod Impact Strength (23°C, 1/8” Notched) | 45.0 | kg-cm/cm | ASTMD256 |
| Tensile Strength at Break (23°C, 5 mm/min) | 360.0 | kg/cm2 | ASTMD638 |
| Tensile Strength at Yield (23°C, 5 mm/min) | 390.0 | kg/cm2 | ASTMD638 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption Equilibrium (23°C/50% RH) | max. 0.3 | wt% | ASTMD570 |
| Mold Shrinkage (60×60×2mm SFlow) | max. 0.4 | wt% | ASTMD955 |
| Rockwell Hardness (23°C, R-scale) | 102.0 | R-scale | ASTMD785 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Unannealing 1.8MPa) | 86.0 | °C | ASTMD648 |
| RTI Elec (1.5 mm) | 60.0 | — | UL 746 |
| RTI Imp (1.5 mm) | 60.0 | — | UL 746 |
| RTI Str (1.5 mm) | 60.0 | — | UL 746 |
| Vicat Softening Temperature (50°C/hr , 1 kg load) | 101.0 | °C | ASTMD1525 |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Arc Resistance | PLC 6 | — | ASTM D495 |
| Comparative Tracking Index | PLC 1 | — | UL 746 |
| Dielictric Strength | 22.0 | KV/mm | ASTM D149 |
| High Amp Arc lgnition (1.5 mm) | PLC 0 | — | UL 746 |
| High Voltage Arc Tracking Rate | PLC 0 | — | UL 746 |
| Hot-Wire Ignition (1.5 mm) | PLC 3 | — | UL 746 |
| Volume Resistivity | 1.0E+16 | Ohm-cm | ASTM D257 |
Table 5 of 7
2 rows| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Flame Rating (1.5 mm) | HB 75 | IEC 60695-11-10,-20 |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 50 - 70 | psi(Mpa) |
| Drying Temperature | 80 - 85 | °C |
| Drying Time | 2.0 - 4.0 | hr |
| Front Zone | 200 - 230 | °C |
| Injection Pressure | Moderately High to high | — |
| Injection Speed | Moderate to Fast | — |
| Melt Zone | 185 - 195 | °C |
| Middle Zone | 210 - 240 | °C |
| Mold Temperature | 40 - 70 | °C |
| Nozzle | 220 - 240 | °C |
| Rear Zone | 200 - 230 | °C |
| Screw Speed | 30 - 100 | rpm |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Rate (200°C, 5kg load) | 1.0 | g/10min | ASTM D1238 |
| Melt Volume Rate (220°C, 10kg load) | 10.0 | g/10min | ASTM D1238 |
| Specific Gravity (23°C) | 1.03 | g/cm3 | ASTM D792 |