To catalogue
fluteck™ C200
- Chemical Family
- Fluoropolymers
fluteck™ C200 PCTFE is a high performance thermoplastic fluoropolymer based on Polychlorotrifluoroethylene
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
- Tooling & Moldmaking
Industrial — Oil, Gas & Mining
- Other Oil Gas & Mining Applications
Electrical & Electronics — Parts & Components
- Other Parts & Components
Electrical & Electronics — Wire & Cable
- Other Wire & Cable Applications
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- fluteck
- Polymer Name
- Ethylene Chlorotrifluoroethylene Copolymer
- Flexural Modulus
- 1500.0 - 1500.0 MPa
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Ball Valves
- Bearings
- Cables
- Filters
- Flanges
- Gaskets
- Oil/Gas Applications
- Pump Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.62 - 1.68 | g/cm³ | ASTM D792 |
| Water Absorption (24 Hours) | max. 0.10 | % | ASTM D570 |
| Mold Shrinkage (Along the Flow) | 2.5 | % | ASTM D955 |
Table 2 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Elongation at Break | min. 200 | % | ASTM D638 |
| Tensile Strength (23°C) | 40 | MPa | ASTM D638 |
| Flexural Strength (Break) | 40 | MPa | ASTM D790 |
| Folding Endurance | 250 x 108 | Cycles | ASTM D2176 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Hardness | D75 | Shore D | ASMT D785 |
| Izod Notched Impact (23°C) | No break | J/m | ASMT D256 |
| Coefficient of Dynamic Friction | 0.2 | — | ASTM D1894 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 222 | °C | ASTM D3418 |
| Max Operating Temperature | 150 | °C | — |
| Flammability Rating | V - 0 | — | UL94 |
| Heat Deflection Temperature (0.45 Mpa) | 90 | °C | ASTM D648 |
| Short Term Service Temperature | - 100 | °C | — |
Table 4 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Constant (1 khz) | 2.48 | — | ASTM D150 |
| Dielectric Strength (23°C, 1.0 mm) | 30 | kV/mm | ASTM D149 |
| Dissipation Factor (1Ghz) | 0.0012 | — | ASTM D150 |
| Arc Resistance | min. 120 | sec | ASTM D495 |
| Volume Resistivity (50% Rh) | min. 10 | Ohm-cm | ASTM D257 |