fluteck™ P1050
- Chemical Family
- Fluoropolymers
fluteck™ P1050 Modified PTFE Standard Grade is Modified PTFE for Ram Extrusion, Compression and Isostatic molding.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- fluteck
- Polymer Name
- Polytetrafluoroethylene (PTFE)
- Processing Methods
Compression Molding, Extrusion, Isostatic Molding, Ram Extrusion
- Color
- White
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Food & Nutrition
- Healthcare & Pharma
- Industrial
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Excellent Transparency Properties
- Good Mechanical Properties
- High Temperature Resistance
- Low Friction
- Low Gas Permeability
- Reduced Friction
- UV Resistant
- Product Properties
- Improved mechanical properties
- Excellent chemical resistance.
- Exceptional temperature resistance
- Excellent electrical insulating properties
- High limiting oxygen index
- Reduced deformation under load
- Higher transparency
- Reduced friction & wear; Low friction behavior
- Handling
Fluteck™ P1050 Modified PTFE Standard Grade can be stored for a long period of life and is exceptionally resistant to aging and weather conditions up to 10 years. Specific aging tests carried out on sample exposed to aging and atmospheric conditions, showed no changes in weight and volume. In case of semi-finished products, before processing or before the machining, it is advisable to store the material for 24 hours in the production area, preferable in a clean and dry place at a temperature of less than 25°C , preferably between 21-25°C. This is very important when room temperature is low; in such cases the material should be conditioned up to 72 hours in the production area in the recommended temperature range
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 2.130 - 2.180 | g/cm³ | ASTM D792 |
| Water Absorption | 0.01 | % | ASTM D570 |
| Flamability | V - 0 | — | UL 94 |
Table 2 of 3
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | min. 28 | MPa | ASTM D4894 |
| Elongation | min. 400 | % | ASTM D4894 |
| Hardness | min. 54 | Shore D | ASTM D2240 |
| Ball Hardness | min. 23 | MPa | ASTM D785 |
| Compression Strength (1% Deformation) | min. 4 | MPa | ASTM D695 |
| Deformation Under Load (140 kg/cm², 24hrs, 23°C) | 9 - 12 | % | ASTM D621 |
| Permanent Deformation (min. 24 Hrs, Relaxation 23°C) | 45 - 6 | % | ASTM D621 |
| Coefficient of Static Friction | 0.08 - 0.10 | — | ASTM D1894 |
| Coefficient of Dynamic Friction | 0.06 - 0.08 | — | ASTM D1894 |
| Wear Factor | 2.9 | — | ASTM D3702 |
| Wear Coefficient | 20000 - 25000 | kgmh | — |
Table 3 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thermal Conductivity | 0.24 | W/mK | ASTM C177 |
| Coefficient of Linear Thermal Expansion (25°C - 100°C) | 12 - 14 | 10⁵/°C | ASTM D696 |
| Dielectric Strength | min. 50 | kV/mm | ASTM D149 |
| Volume Resistivity | 10¹⁸ | Ohm-cm | ASTM D257 |
| Surface Resistivity | 10 | Ohm | ASTM D257 |