NORYL™ Resin NH7010HV
SABIC's Specialties Business NORYL NH7010HV resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm along with a UL746C Outdoor Suitability rating of F1. NORYL NH7010HV resin is a higher flow version of NH7010 resin and offers a good balance of affordable high heat, flow, hydrolytic stability, excellent creep resistance, dimensional stability. This material is a good candidate for outdoor housings / enclosures and photovoltaic / solar junction box applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Artificial Turf
- Consumer Electronics
- Displays
- Connectors
- Switches & Relays
- Renewable Energy
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1090.0 - 1090.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Impact Modifier
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Good Processability
- High Flow
- High Flowability
- High Hydrolytic Stability
- High Impact Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Energy Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 59 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 12 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2180 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 100 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2460 | MPa | ASTM D790 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.09 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 20.1 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.09 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.25 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.05 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 20 | cm³/10 min | ISO 1133 |
Table 3 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 159 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 139 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00008 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 8.00E-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00008 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (approximate maximum) ¹¹ | 145 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 162 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 139 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 0.75 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 227 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 69 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 53 | J | ASTM D3763 |
Table 6 of 7
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 110 - 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0 | % |
| Melt Temperature ⁷ | 300 - 325 | °C |
| Nozzle Temperature ⁷ | 300 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 290 - 325 | °C |
| Middle - Zone 2 Temperature ⁷ | 275 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 315 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 20 - 100 | rpm |
Table 7 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ʳ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ʳ | 9.60E+02 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
| UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |