NORYL™ Resin EX130
SABIC's Specialties Business NORYL™ EX130 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection molding grade exhibits a good balance of impact resistance and surface esthetics. NORYL™ EX130 resin, with its low warpage and dimensional stability, is an excellent candidate for automotive exterior applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Automotive Lighting
- Exterior & Body
- Interior Fixtures
- Lighting
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1060.0 - 1060.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Flexural Modulus
- 2160.0 - 2160.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Amorphous
- Dimensional Stability
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Low Warpage
- No Added PFAS
- Country Availability
- China (Mainland)
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Electrical/Electronic Applications
- Lighting Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 4.6 | g/10 min | ASTM D1238 |
| Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.06 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 53 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 50 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 78 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2160 | MPa | ASTM D790 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 127 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000055 - 0.000075 | 1/°C | TMA |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 235 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.5 - 1.4 | MPa |
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Front - Zone 3 Temperature ⁷ | 270 - 310 | °C |
| Melt Temperature ⁷ | 275 - 310 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 300 | °C |
| Mold Temperature ⁷ | 70 - 110 | °C |
| Nozzle Temperature ⁷ | 270 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 245 - 290 | °C |
| Screw Speed ⁷ | 40 - 60 | rpm |