NORYL™ Resin PX1860
SABIC's Specialties Business This injection moldable grade offers improved hydrolytic stability, very low moisture absorption, heat / hot water resistance and was developed for water management applications. NORYL PX1630 has been certified for potable water applications up to 85C in Europe and North America in limited colors. *NSF certification is color dependent.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Equipment & Parts
- Consumer Electronics
- Displays
- Connectors
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Material Features
- Amorphous
- Dimensional Stability
- Flame Retardant
- Heat Stabilized
- High Hydrolytic Stability
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Connectors
- Displays
- Electrical/Electronic Applications
- Electronic Components
- Tablets
- Washing Machine
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 52 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 49 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 3.6 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 7.3 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 3140 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 98 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2770 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 53 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 3.5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2510 | MPa | ISO 527 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.13 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.02 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 2.16 kg) ¹¹ | 34 | cm³/10 min | ISO 1133 |
| Density ¹¹ | 1.1 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 280°C, 1.2 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
Table 3 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000074 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000074 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000074 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000074 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 110 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 111 | °C | ISO 306 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 90 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 114 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 92 | °C | ISO 75/Af |
Table 4 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 4.00E+16 | Ω.cm | ASTM D257 |
| Volume Resistivity ¹¹ | 4.00E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity ¹¹ | 1.00E+14 | Ω | ASTM D257 |
| Surface Resistivity (ROA) ¹¹ | 1.00E+14 | Ω | IEC 60093 |
| Comparative Tracking Index ʳ ¹¹ | 250 | V | IEC 60112 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.02 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.02 | — | IEC 60250 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 28.6 | kV/mm | IEC 60243-1 |
Table 5 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 38 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 27 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6 | kJ/m² | ISO 179/1eA |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 70 - 80 | °C |
| Drying Time ⁷ | 2 - 3 | Hrs |
| Melt Temperature ⁷ | 260 - 295 | °C |
| Nozzle Temperature ⁷ | 250 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 260 - 295 | °C |
| Middle - Zone 2 Temperature ⁷ | 240 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 210 - 230 | °C |
| Hopper Temperature ⁷ | 65 - 85 | °C |
| Mold Temperature ⁷ | 45 - 70 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ʳ ᵖ | 3 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) ᵖ | 30 | % | ISO 4589 |