Staramide™ PF00A
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break (5 mm/min) | 220 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 3 | % | ISO 527 |
| Flexural Modulus (2 mm/min) | 13200 | MPa | ISO 178 |
| Flexural Stress at Break (2 mm/min) | 300 | MPa | ISO 178 |
| Izod Notched Impact Strength (80x10x4, 23°C) | 12 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 80 | kJ/m2 | ISO 180/1U |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar - Flow | 0.1 - 0.2 | % | E2P Method |
| Moisture Absorption (23°C / 50% rh) | 0.6 | % | ISO 62 |
| Water Absorption (23°C/Sat) | 4.5 | % | ISO 62 |
| Density | 1.55 | g/cm3 | ISO 1183/A |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm) | 210 | °C | ISO 75/Ae |
| Ball Pressure Test (125°C +/ - 2°C) | PASSES | °C | IEC 60695-10-2 |
Table 4 of 4
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Maximum Moisture Content | 0.2 | % |
| Melt Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Mold Temperature | 50 - 90 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |