To catalogue
Staramide™ PF006S
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (1 mm/min) | 9500 | MPa | ISO 527 |
| Tensile Stress at Break (5 mm/min) | 160 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 3.7 | % | ISO 527 |
| Flexural Modulus (2 mm/min) | 8000 | MPa | ISO 178 |
| Flexural Stress at Break (2 mm/min) | 230 | MPa | ISO 178 |
| Charpy V - Notch Edge (-30°C, 80x10x4 Sp=62 mm) | 9 | kJ/m2 | ISO 179/1eA |
| Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 11 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotch Edge (-30°C, 80x10x4 Sp=62 mm) | 75 | kJ/m2 | ISO 179/1eU |
| Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 90 | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (80x10x4, - 20°C) | 10 | kJ/m2 | ISO 180/1A |
| Izod Notched Impact Strength (80x10x4, - 30°C) | 9 | kJ/m2 | ISO 180/1A |
| Izod Notched Impact Strength (80x10x4, - 40°C) | 9 | kJ/m2 | ISO 180/1A |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar - Flow | 0.8 - 1.1 | % | E2P Method |
| Moisture Absorption (23°C / 50% rh) | 1.8 | % | ISO 62 |
| Water Absorption (23°C/Sat) | 6.5 | % | ISO 62 |
| Density | 1.37 | g/cm3 | STANDARD ISO 1183 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm) | 205 | °C | ISO 75/Ae |
| HDT/Be (0.45MPa Edge 120x10x4 Sp=100mm) | 220 | °C | ISO 75/Be |
| Coefficient of Thermal Expansion - Flow (23°C to 60°C) | 2.5e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion - Xflow (23°C to 60°C) | 8.5e-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/50) | 215 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) | 215 | °C | ISO 306 |
| Ball Pressure Test (125°C +/ - 2°C) | PASSES | °C | IEC 60695-10-2 |
| Thermal Conductivity | 0.33 | W/m/K | ISO 22007-2 |
Table 4 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity (ROA) | min. 1.E+16 | ohm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.4 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) | 3.6 | — | IEC 60250 |
| Comparative Tracking Index - CTI | 500 | V | UL 746 |
| Dissipation Factor (1 MHz) | 0.016 | — | ASTM D 150 |
| Dissipation Factor (50/60 Hz) | 0.0061 | — | IEC 60250 |
| Dielectric Strength (Oil, 3.2 mm) | 20 | kV/mm | IEC 60243-1 |
| Volume Resistivity | min. 1.E+16 | ohm.m | IEC 60093 |
Table 5 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glow Wire Flammability Index - GWFI (Passes at 650°C) | 2 | mm | IEC 60695-2-12 |
| Oxygen Index - LOI | 25 | % | ISO 4589 |
| Fmvss Burning Speed (2 mm) | 6 | mm/min | FMVSS 302 |
| Fmvss Burning Speed (3 mm) | 2 | mm/min | FMVSS 302 |
| Ul E2P Measurement, 94HB Flame Class Rating | 0.75 | mm | UL 94 |
Table 6 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | — |
| Mold Temperature | 60 - 80 | °C | -- |
| Drying Time | 4.0 - 6 | hrs | — |
| Front - Zone 3 Temperature | 240 - 270 | °C | — |
| Maximum Moisture Content | 0.2 | % | — |
| Melt Temperature | 240 - 270 | °C | — |
| Middle - Zone 2 Temperature | 240 - 250 | °C | — |
| Rear - Zone 1 Temperature | 230 - 240 | °C | — |