Starflam™ RF0068E
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Starflam
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Flame Retardant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain at Break | 2.4 | % | ASTM D 638 |
| Flexural Modulus (2 mm/min) | 8000 | MPa | ISO 178 |
| Flexural Stress at Yield (2 mm/min) | 180 | MPa | ISO 178 |
| Izod Notched Impact Strength (80x10x4, 23°C) | 7 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 40 | kJ/m2 | ISO 180/1U |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (24 h) | 0.2 - 0.5 | % | ISO 294 |
| Water Absorption (23°C/24 h) | 0.2 | % | ISO 62-1 |
| Density | 1.42 | g/cm3 | STANDARD ISO 1183 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 225 | °C | ISO 75/Af |
| Relative Temperature Index - Electrical | 140 | °C | UL 746B |
| Relative Temperature Index - Mechanical With Impact | 105 | °C | UL 746B |
| Relative Temperature Index - Mechanical Without Impact | 140 | °C | UL 746B |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| High Ampere Arc Ign (Surface, PLC) | 0 | — | UL 746A |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glow Wire Flammability Index - GWFI (Passes at 960°C) | 0.8 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature - GWIT (1.0 mm) | 725 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature - GWIT (3.0 mm) | 750 | °C | IEC 60695-2-13 |
| Ul Recognized, 94V - 0 Flame Class Rating | 0.8 | mm | UL 94 |
Table 6 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 80 | °C | — |
| Mold Temperature | 60 - 100 | °C | -- |
| Drying Time | 4 | hrs | — |
| Front - Zone 3 Temperature | 270 - 280 | °C | — |
| Maximum Moisture Content | 0.15 - 0.25 | % | — |
| Melt Temperature | 270 - 280 | °C | — |
| Middle - Zone 2 Temperature | 270 - 280 | °C | — |
| Rear - Zone 1 Temperature | 265 - 275 | °C | — |