Star L™ PS D18
- Chemical Family
- Styrenics
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Star L
- Polymer Name
- Polystyrene (unspecified)
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Lubricated
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Yield (5 mm/min) | 33 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | min. 20 | % | ISO 527 |
| Flexural Modulus (2 mm/min) | 3200 | MPa | ISO 178 |
| Flexural Stress at Yield (2 mm/min) | 48 | MPa | ISO 178 |
| Izod Notched Impact Strength (80x10x4, 23°C) | 2.5 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 19 | kJ/m2 | ISO 180/1U |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (4mm) | 0.4 - 0.6 | % | E2P Method |
| Density | 1.07 | g/cm3 | ISO 1183 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 75 | °C | ISO 75/Af |
Table 4 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Temperature | 60 - 80 | °C | -- |
| Drying Temperature | 70 | °C | — |
| Drying Time | 3 | hrs | — |
| Front - Zone 3 Temperature | 190 - 225 | °C | — |
| Melt Temperature | 190 - 225 | °C | — |
| Middle - Zone 2 Temperature | 190 - 225 | °C | — |
| Rear - Zone 1 Temperature | 190 - 225 | °C | — |