Nylon 6 MoS2 Extruded Sheet
- Chemical Family
- Polyamides
PAR Group Nylon 6 MoS2 Extruded Sheet offers increased load bearing and wear resistance, whilst maintaining the impact and fatigue resistance of standard nylon grades. It is self-lubricating, electrically insulating and has a high fatigue resistance. We also manufacture our own brand of Corromide® CMF (Nylon 6 Sheet - MoS2 Filled Cast) in sheets, rods and tubes. Our MoS2 Filled Cast Nylon 6 is available in greater sheet thicknesses and offers a higher temperature rating compared to MoS2 Filled Extruded Nylon 6. Nylon 6 Sheet - MoS2 Filled Extruded is available to buy online at PAR Direct by clicking the link above.
Properties
- Physical Form
- Sheets
Product families
- Equipment & Parts
- Other Industrial Applications
- Other Parts & Components
- Terminal Blocks Plugs & Sockets
Other characteristics
- Brand
- PAR Group Nylon 6
- Color
- Black
- Density
- 1140.0 - 1140.0 kg/m³
- Features
Chemical Resistant, Electrically Insulating, Fatigue Resistant, Good Abrasion Resistance, Good Machinability, Good Stiffness, High Hardness, High Impact Resistance, High Strength, Self Lubricating, Temperature Resistance, Wear Resistant
- Polymer Name
- Polyamide 6 (PA 6)
- Tensile Modulus
- 3200.0 - 3200.0 MPa
- Markets
- Electrical & Electronics
- Industrial
- Availability
- Yes denotes available No denotes unavailable
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Product Families
- Plastics — Parts, Shapes & Films
- Additives Included
- Lubricant (Molybdenum Disulfide)
- Material Features
- Chemical Resistant
- Electrically Insulating
- Fatigue Resistant
- Good Abrasion Resistance
- Good Machinability
- Good Stiffness
- High Hardness
- High Impact Resistance
- Key Features
Temperature: -40°C up to +85°C.; Electrically insulating.; High resistance to fatigue and self-lubricating.; Offers improved wear resistance compared to standard extruded Nylon 6 grades.; Easily machined.
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Bearings
- Gears
- Industrial Connectors
- Pulleys
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Yield Stress | 80 | MPa | DIN EN ISO 527 |
| Elongation at Break | min. 50 | % | DIN EN ISO 527 |
| Tensile Modulus of Elasticity | 3200 | MPa | DIN EN ISO 527 |
| Notched Impact Strength (Charpy) | min. 3.0 | kJ/m2 | DIN EN ISO 179 |
| Ball Indentation | 170 | MPa | DIN EN ISO 2039-1 |
| Shore D | 82 | Scale D | DIN EN ISO 868 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.14 | g/cm3 | DIN EN ISO 1183-1 |
| Water Absorption | 3 | % | DIN EN ISO 62 |
Table 3 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 220 | °C | ISO 11357-3 |
| Thermal Conductivity | 0.23 | W/(m*K) | DIN 52612-1 |
| Thermal Capacity | 1.7 | kJ/(kg*K) | DIN 52612 |
| Coefficient of Linear Thermal Expansion | 90 | 10-6K-1 | DIN 53752 |
| Service Temperature - Long Term | -40 up to 85 | °C | Average |
| Service Temperature - Short Term | max. 160 | °C | Average |
| Heat Deflection Temperature | 75 | °C | DIN EN ISO 75, Method A |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flammability (Thickness 3mm/6mm) | HB / HB | UL 94 |