Nylon 6 Cast Natural Sheet
- Chemical Family
- Polyamides
PAR Group Nylon 6 Cast Natural Sheet is a common engineering plastic due to its ease of machinability. It combines high strength, stiffness and hardness properties with good creep and wear resistance. Nylon 6 Sheet - Cast Natural also has good heat aging properties, is electrically insulating and is resistant to the majority of oils, chemicals, fuels and cleaning fluids. Below shows the standard sheet availability, many of which, are manufactured in-house utilizing our own Nylon Casting facilities. Many of these are available to buy online by clicking the link above. We can also manufacture large sheets, rods, tubes or bespoke shapes. Nylon 6 Sheet - Cast Natural is available to buy online at PAR Direct by clicking the link above.
Properties
- Physical Form
- Sheets
Product families
- Equipment & Parts
- Other Industrial Applications
- Other Parts & Components
- Terminal Blocks Plugs & Sockets
Other characteristics
- Brand
- PAR Group Nylon 6
- Color
- Natural
- Density
- 1145.0 - 1145.0 kg/m³
- Features
Chemical Resistant, Creep Resistant, Electrically Insulating, Good Abrasion Resistance, Good Machinability, Good Sliding Properties, Good Stiffness, Heat Aging Resistant, High Hardness, High Impact Resistance, High Strength, Wear Resistant
- Polymer Name
- Polyamide 6 (PA 6)
- Markets
- Electrical & Electronics
- Industrial
- Availability
- Yes denotes available No denotes unavailable
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Chemical Resistant
- Creep Resistant
- Electrically Insulating
- Good Abrasion Resistance
- Good Machinability
- Good Sliding Properties
- Good Stiffness
- Heat Aging Resistant
- Key Features
Temperature: -40°C up to +100°C.; High strength and stiffness.; Good impact and wear resistance.; Good sliding properties and resistance to abrasion.; Good resistance to chemicals and oils.; Easily machined.
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Bearings
- Gears
- Industrial Connectors
- Pulleys
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (Sample Type 1B, 50mm min^-1) | 80 (11603) | MPa / psi | ISO 527-1/2:1993 |
| E-modulus (Sample Type 1B, 50mm min^-1) | 4000 (580152) | MPa (psi) | ISO 527-1/2:1993 |
| Elongation at Break (Sample Type 1B, 50mm min^-1) | min. 20 | % | ISO 527-1/2:1993 |
| Compressive Strength (Sample Type B, 5mm min-) | 95 (13779) | MPa (psi) | ISO 604:2002 |
| Compressive Modulus (Sample Type A, 1mm min^-1) | 2700 (391603) | MPa (psi) | ISO 604:2002 |
| Flexural Strength (1.5mm min^-1) | 105 / 15229 | MPa (psi) | ISO 178:2001 |
| Flexural Modulus (1.5mm min^-1) | 3300 / 478626 | MPa (psi) | ISO 178:2001 |
| Izod Impact Strength (Sample Type A (Notched)) | 5.60 (2.66) | KJ/m2 ( ft.lb/in2 ) | ISO 180:2000 |
| Hardness | 84 | Shore D | ISO 868:2003 |
| Coefficient of Friction (Dynamic, 31.4m/min, 1.75MPa) | 0.39 | — | — |
| Wear Rate (31.4m/min, 1.75MPa) | 0.44 | mg/km | — |
| K-Factor (31.4m/min, 1.75MPa) | 5.0x10^-6 (2.4x10^-9) | mm3/Nm ( in3.min./ft.lb.hr ) | — |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.145 (0.041) | g/cm3 (lb/inch3) | ISO1183:1987 |
| Water Absorption (24 hours, Immersion, 23°C) | 0.3 | % | ISO 62:1999 (modified) |
| Water Absorption (Saturation, Immersion, 23°C) | 7 | % | ISO 62:1999 |
Table 3 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 220 (428) | °C (°F) | — |
| Max. Intermittent Service Temp | 170 (338) | °C (°F) | — |
| Max. Continuous Service Temp (5000hrs) | 100 (212) | °C (°F) | — |
| Min. Intermittent Service Temp. | -100 (-148) | °C (°F) | — |
| Min. Continuous Service Temp. | -40 (-40) | °C (°F) | — |
| Coefficient of Linear Thermal Expansion (TMA,23°C to 55°C) | 8x10^-5 (4.44x10^-5) | °C-1 (°F-1) | ISO 11359-2:1999 |
| Thermal Conductivity (Mean T = 20°C) | 0.26 (0.15) | W/m.°C (BTU in/ft.hr.°F) | ISO 8301:1991 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Constant (1MHz) | 3.7 | — | IEC 60250:1969-01 |
| Dielectric Constant (Low Frequency,100Hz) | 4 | — | — |
| Dielectric Strength | 25 (635) | kV/mm (Kv/in) | IEC 60243-1:1998-01 |
| Volume Resistivity | 1x10^13 (3.93x10^14) | ohm.m (ohm.in) | IEC 60093:1980-01 |
| Surface Resistivity ROA | 1x10^12 | ohm | IEC 60093:1980-01 |
| Comparative Tracking Index | 600 | CTI | IEC 60112:2003-01 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Flammability | HB | IEC 60695-11-10:2003-08 |