To catalogue
Chartwell C-515.71HR
- CASE Ingredients Features
- Excellent Creep ResistanceLow BlisteringPeel ResistanceSalt Resistance
- Chemical Family
- Organometallics
An increased reactivity amino functional metal organic adhesion promoter synthesized with a stabilized neutralized metal complex. The product is supplied as a solution in propylene glycol.
Properties
- Physical Form
- Liquid
Identification
- CASE Ingredients Functions
- Adhesion PromoterCoupling Agent
Product families
Applications
Adhesives & Sealants — Building & Construction
- Construction Adhesives
Paints & Coatings — Building & Construction
- Concrete Coatings & Stains
- Wood Coatings & Finishes
Building & Construction — Building Materials
- Construction Adhesives
Industrial — Chemical & Industrial Manufacturing
- Ceramics & Refractory
Paints & Coatings — Industrial Coatings
- Metal Coatings
Product Families
CASE Ingredients — Additives
- Functional Additives
Other characteristics
- Brand
- Chartwell
- End Uses
- Primer, Waterborne Coating
- Features
Excellent Creep Resistance, Low Blistering, Peel Resistance, Salt Resistance
- Functions
- Adhesion Promoter, Coupling Agent
- Compatible Polymers & Resins
Acrylics, Alkyds, Epoxies (EP), Polyurethanes (PU)
- Carrier
- Propylene Glycol
- Solvent-based
- Markets
- Adhesives & Sealants
- Building & Construction
- Industrial
- Paints & Coatings
- Procedure
- 1. Water-Borne
- Post add at 0.35 - 1.4 wt% on polymer solids. Mix with conventional paddle-type mixer.
- 2. 2K Epoxy and 2K Urethane
- Optimum performance is achieved when added to the hardener (epoxies) or polyol (urethanes). Product must be high shear mixed with a Cowles type mixer. Milling alone is not sufficient. Use Level 0.35 - 1.4 wt% on polymer solids.
- Use Levels
- 0.35 - 1.4 wt%
- Application
- Coatings, Adhesives & Inks
- Will improve adhesion to all metals with acccompanying improved salt fog resistance, reduction of creep at the scribe, and reduced blistering, and improved adhesion to ceramics, concrete, wood and plastics (except untreated PP/ PE). In WB exterior primers and deck stains, will eliminate peeling on wood substrate. In foundry cores, will improve bonding between sand and phenolic, urethane and similar binders.
- Water-Borne Coatings
- For acrylic, styrenated acrylic, phenolic, PUD and alkyd coatings having pH 7-11. Use level 0.35 - 1.4 wt per cent on polymer solids.
- 2K Epoxy and 2K Urethane
- Always add to hardener (epoxies) or polyol (urethanes). Use leve l0.35 - 1.4 wt. per cent on polymer solids.
- Urethane modified nitrocellulose
- Add with Cowles-type mixing for 10 minutes. Use level 0.35 - 1.4 wt per cent based upon binder solids.
- Coating Type
- Primer
- Waterborne Coating
- Technology
- CASE Ingredients
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ECL (Korea)
- IECSC (China)
- KECI (Korea)
- TCSI (Taiwan)
- TSCA (USA)
- Certifications and Compliance
Comprehensive Environmental Response Compensations & Liability Act (CERCLA); REACH (Europe)
- Compatible Polymers and Resins
- Acrylics
- Alkyds
- Epoxies (EP)
- Polyurethanes (PU)
- Compatible Substrates and Surfaces
- Ceramic
- Concrete
- Metal
- Plastics
- Wood
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Active Matter Content | 41.5 | wt% |
| Complexed Organics | 25.6 - 26.4 | — |
| pH Value (1% Solution) | 7.5 | — |
| Specific Gravity | 1.23 | g/ml |
| Total Metal Content | 7.3 - 7.9 | % |
| Neutralizing Agent | Caustic | — |
| Organofunctionality | Amino | — |