Chartwell B-515.1
- CASE Ingredients Features
- Corrosion ResistanceExcellent DispersibilityExcellent SolubilityGood Moisture ResistanceHeat ResistancePeel Resistance
- Chemical Family
- Organometallics
An amino functional metal organic adhesion promoter synthesized using a stabilized bimetal precursor. The product is supplied in ethylene glycol to aid in rapid dispersion and solubilization of the active components in polymer matrices.
Properties
- Physical Form
- Liquid
Identification
- CASE Ingredients Functions
- Adhesion PromoterCoupling Agent
Product families
Applications
Paints & Coatings — Industrial Coatings
- Metal Coatings
Product Families
CASE Ingredients — Additives
- Functional Additives
Elastomers — Elastomer Additives
- Surface Modifiers
Plastics — Polymer Additives
- Surface Modifiers
Other characteristics
- Brand
- Chartwell
- Features
Corrosion Resistance, Excellent Dispersibility, Excellent Solubility, Good Moisture Resistance, Heat Resistance, Peel Resistance
- Functions
- Adhesion Promoter, Coupling Agent
- Compatible Polymers & Resins
Acrylics, Alkyds, Epoxies (EP), Latex, Phenolic Resins, Polyesters, Polyurethanes (PU)
- Carrier
- Ethylene Glycol
- Solvent-based
- Markets
- Paints & Coatings
- Procedure
- HIGH SHEAR MIXING NECESSARY IN ALL SOLVENT-BORNE SYSTEMS
- 1. Coatings/ Inks
- Optimum performance is achieved when added directly to the grind stage resin and high shear mixed for 15 mins before adding other components. Must be high shear mixed with a Cowles type mixer. Milling alone is not sufficient.
- Two component epoxies
- Add to resin (A side); level is 1.0 - 2.0 wt. per cent of total binder (combined resin + hardener)
- Two component urethanes
- Add to polyol (B side); level is 1.0 - 2.0 wt. per cent of total binder (combined isocyanate +polyol).
- 2. Adhesives
- 1.0-2.0 phr, post add recommended under agitation
- 3. Plastics
- 1.0-2.0 phf (parts per hundred filler; recommend pretreat of pigments/ fillers in a Henschel or similar mixer and subsequently compound with resin. For high surface area pigments/ fillers, ie fumed silica, carbon black, phthalo, and similar.
- 4. Rubber
- 1.0-3.0 phr, add directly onto silica or other filler and compound in a Banbury mixer.
- Application
- (1) Adhesives
- Recommended for epoxy, urethane, and rubber adhesives to enhance adhesion to metals, plastics and elastomers. Increased T-peel strength. Improved resistance to moisture, heat and corrosive environments.
- (2) Coatings
- Recommended for enhancing adhesion of epoxy, urethane, alkyd, acrylic, polyester and other solvent-borne coatings to metal surfaces with resultant reduction in corrosion. Also enhances adhesion to many plastic surfaces. Useful in most water-borne coatings (Latex and polymer dispersion) for enhanced adhesion to metal and plastic substrates.
- Coating Type
- Latex
- Waterborne Coating
- Technology
- CASE Ingredients
- Elastomers
- Plastics
- Adhesive & Sealant Type
- Epoxy Adhesive
- Compatible Polymers and Resins
- Acrylics
- Alkyds
- Epoxies (EP)
- Latex
- Phenolic Resins
- Polyesters
- Polyurethanes (PU)
- Plastics and Elastomers Functions
- Adhesion Promoter
- Compatible Substrates and Surfaces
- Elastomers & Rubbers
- Metal
- Plastics
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Active Matter Content | 25.5 | wt% |
| Complexed Organics | 9.1-9.3 | — |
| Specific Gravity | 1.23 | g/ml |
| Total Metal Content | 5.2 - 5.9 | % |
| Organofunctionality | Amino | — |
| pH Value (2% Solution) | 4.5 | — |