TABOREN® PH 52 G 20-094
- Chemical Family
- PolyolefinsPolypropylenes (PP)
TABOREN-PH 52 G 20-094 is a compound based on polypropylene homopolymer, filled with 20% of short glass fibers and stabilized with a basic additive package. It is desinged for injection molding technology and used in automotive applications without high demands on performance under enhanced temperatures. The grade is available in standard black color.
Product families
Applications
- Interior
Product Families
- Polyolefins
Other characteristics
- Brand
- TABOREN
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 5.0 - 5.0 g/10 min
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Safety
TABOREN-PH 52 G 20 -094 is not classified as a dangerous preparation.
- Markets
- Automotive & Transportation
- Recycling
The product is suitable for recycling using modern methods of shredding and cleaning.
- Processing
- Drying
- TABOREN-PH 52 G 20-094 is recommended to be pre-dried before processing. A guideline is to dry the grade at 80°C for 3 hrs.
- Machine Requirements
- TABOREN-PH 52 G 20-094 is easy to process on standard injection molding machines. The following molding parameters are to be used as guidelines: Melt Temperature: 200 - 250 °C Injection Speed: Medium Injection Pressure: 90 - 130 MPa Hold-on Pressure: >40% of injection pressure Mold Temperature: 30 - 50 °C
- Technology
- Plastics
- Material Features
- Homopolymer
- Recyclable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Storage and Handling
TABOREN-PH 52 G 20-094 should be stored in dry conditions at temperatures below 50°C and protected from UV light. Improper storage may initiate degradation resulting in odor generation and color changes a can have negative effects on the physical properties of the product.
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index (230°C / 2.16 kg) | 5 | g/10 min | ISO 1133 |
| Density | 1.05 | g/cm³ | ISO 1183-1 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 75 | MPa | ISO 527 |
| Elongation at Break | 4 | % | ISO 527 |
| Flexural Modulus | 4000 | MPa | ISO 178 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CHARPY Notched Impact Strength | 8 | kJ/m² | ISO 179-1/1eA 23°C |
| CHARPY Unnotched Impact Strength | 40 | kJ/m² | ISO 179-1/1eU 23°C |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Temperature | 162 | °C | ISO 306, method A50 |