TABOREN® PR 65 T 10S-089
- Chemical Family
- PolyethylenesPolyolefinsPolypropylenes (PP)
TABOREN® PR 65 T 10S-089 is a PP/PE, Filler: Mineral filler, Stabilization: Antioxidant + UV + Anti-scratch
Product families
Applications
Applications
- Industrial — Other Industrial Applications
Automotive & Transportation — Automotive
- Interior
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- TABOREN
- Density
- 980.0 - 980.0 kg/m³
- Polymer Name
- PP/HDPE Alloy
- Flexural Modulus
- 1300.0 - 1300.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Industrial
- Technology
- Plastics
- Fillers Included
- Talc
- Additives Included
- UV Stabilizer
- Material Features
- Good Processability
- Good Scratch Resistance
- High Density
- Recyclable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate | 13 | g/10min | ISO 1133 230°C, 2.16 kg |
| Density | 0.98 | g/cm³ | ISO 1183-1 |
| Tensile Stress at Yield | 17 | MPa | ISO 527 |
| Elongation at Break | 40 | % | ISO 527 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| CHARPY Notched Impact Strength | 20 | kJ/m² | ISO 179-1/1eA 23°C |
| CHARPY Unnotched Impact Strength | No Break | kJ/m² | ISO 179-1/1eU 23°C |
| VICAT Softening Temperature | 130 | °C | ISO 306 method A50 |