TABOREN® PH 89 T 20-075
- Chemical Family
- PolyolefinsPolypropylenes (PP)
TABOREN-PH 89 T 20-075 is a compound based on polypropylene homopolymer filled with 20% of talc, stabilized with a high antioxidant package. It is designed for injection molding technology and used in many industrial fields with stress put on excellent processability and good surface performance. The grade is available in black color.
Product families
Applications
- Industrial — Other Industrial Applications
- Interior
- Other Automotive Applications
- Equipment & Parts
Product Families
- Polyolefins
Other characteristics
- Brand
- TABOREN
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 15.0 - 15.0 g/10 min
- Fillers Included
- Talc
- Processing Methods
- Injection Molding
- Safety
TABOREN-PH 89 T 20-075 is not classified as a dangerous preparation.
- Markets
- Automotive & Transportation
- Industrial
- Recycling
The product is suitable for recycling using modern methods of shredding and cleaning.
- Technology
- Plastics
- Material Features
- Homopolymer
- Recyclable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Storage and Handling
TABOREN-PH 89 T 20-075 should be stored in dry conditions at temperatures below 50°C and protected from UV light. Improper storage may initiate degradation resulting in odor generation, color changes and could have negative effects on the physical properties of the product.
- Processing Guidelines
- Drying
- TABOREN-PH 89 T 20-075 is recommended to be pre-dried before processing. A guideline is to dry the grade at 80°C for 3 hrs.
- Machine Requirements
- TABOREN-PH 89 T 20-075 can be processed without problems on standard molding machines. The following molding parameters are to be used as guidelines: Melt Temperature: 200 – 250°C Injection Speed: Medium Injection Pressure: 90 – 130 MPa Hold-on Pressure: ˃40% of injecƟon pressure Mold Temperature: 30 - 50°C
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index (230°C / 2.16 kg) | 15,0 | g/10 min | ISO 1133 |
| Density | 1050 | g/cm³ | ISO 1183-1 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 30 | MPa | ISO 527 |
| Charpy Notched Impact Strength | 2,5 | kJ/m² | ISO 179-1/1eA 23°C |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179-1/1eU 23°C |
| Elongation at Break | 10 | % | ISO 527 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Temperature | 154 | °C | ISO 306 method A50 |