Hitac Adhesives and Coatings RA-15W

Other characteristics

End Uses

Pressure Sensitive Adhesive

Functions

Release Agent

Labeling Claims

Other Labeling Claims

Compatible Polymers & Resins

Polyesters, Vinyl Esters

Carrier

Water

Markets

• Adhesives & Sealants
• Printing & Packaging

Appearance

Clear to slightly hazy, Clear To Slightly Hazy

Technology

CASE Ingredients

HIGHLIGHTS

RA-15W is an enhanced release version of RA-13W that has been commercially available for many years. Its release properties are virtually identical to carbamate PVODC and yield easy-to-moderate unwind in standard and premium packaging tapes, and filament tapes. It is also effective in release for polyethylene-backed diaper fastening tapes with adhesives based on SIS block copolymers, SIS/SBR, SBR, natural rubber, and acrylics. The release is also effective in polyester, vinyl, and filament tape constructions. Polypropylene and polyethylene films should be free of any lubricants or other surface-finishing materials and must be corona treated to 38 dyne/cm or higher to obtain effective release. Coater-ready solutions are easily prepared by mixing RA-15W with water, (deionized if the local water supply is too hard) to 0.5-5% total solids, depending on the adhesive, substrate and coating method, which can be Meyer bar #3-12, Anilox and rotogravure roll #160-350. The following is a recommendation for initial laboratory evaluation: Coat the film placed on a glass plate with a 2% T.S. solution of RA-15W using a #6 Meyer rod and dry horizontally in air oven at 150ºF (65ºC) for 10 minutes or until completely dry. This may be followed by a pilot coater trial or production evaluation. Unlike silicone release agents, crosslinking is neither necessary nor occurring on drying or tape storage. Release properties develop by simply flashing off the water in a production oven at 120-250ºF (50-120ºC), depending on substrate, web speed, oven length, dry air temperature, dry air velocity, and other configurations. These properties allow release coating and adhesive coating in a single step. It is important to achieve complete drying. Use the highest possible drying temperature to maximize the running speed. The coating is dry when the film is clear and resists moderate finger rub.

Show in full

Unwind Adhesion Value

BASED ON PREMIUM OPP PACKING TAPE WITH SIS-BASED PSA

Adhesive & Sealant Type

Pressure Sensitive Adhesive

Compatible Polymers and Resins

• Polyesters
• Vinyl Esters

Initial Laboratory Evaluation

Coat the film placed on a glass plate with a 2% T.S. solution of RA-15W using a #6 Meyer rod and dry horizontally in air oven at 150ºF (65ºC) for 10 minutes or until completely dry. This may be followed by a pilot coater trial or production evaluation.