EPLAMID 6 GFC 30 NC Q1B0C001
- Chemical Family
- Polyamides
Polyamide 6, reinforced with 30% of glass fiber and glass spheres, heat stabilized and lubricated for injection molding.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- EPLAMID
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Ball, Glass Fiber
- Glass Ball
- Glass Fiber
- Flexural Modulus
- 5500.0 - 5500.0 MPa
- Processing Methods
- Injection Molding
- Notes
Eplamid 6 glass fiber and glass sphere compounds offer a very good surface finish, dimensional stability as well as good all around mechanical properites which are used in many sectors of industry.This material is available in natural and colors on request.
- Markets
- Industrial
- Technology
- Plastics
- Material Features
- Dimensional Stability
- Good Mechanical Properties
- Good Surface Finish
- Heat Stabilized
- Lubricated
- Plastics and Elastomers End Uses
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Unnotched izod impact (23°C) | 25 | kJ/m² | ISO 180/1U |
| Flexural modulus (2mm/min) (23°C) | 5500 | MPa | ISO 178 |
| Flexural strength (2mm/min) (23°C) | 170 | MPa | ISO 178 |
| Tensile modulus (1mm/min) (23°C) | 6600 | MPa | ISO 527-2 |
| Tensile strain at break (5mm/min) (23°C) | 3 | MPa | ISO 527-2 |
| Tensile stress at break (5mm/min) (23°C) | 120 | MPa | ISO 527-2 |
| Unnotched charpy impact (23°C) | 45 | kJ/m² | ISO 179/1eU |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold shrinkage- parallel/normal (3mm) | 0,5/0,9 | % | ISO 294-4 |
| Ash content | 30 | % | ISO 3451-4 |
| Density (23°C) | 1,34 | g/cm3 | ISO 1183 |
| Determination of water content | 0,1 | % | ISO 1183 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temp. of deflection under load (1,80 MPa) | 200 | °C | ISO 75-2/A |
| Melting point | 220 | °C | ISO 3146 |
| Notched charpy impact (23°C) | 7 | kJ/m² | ISO 75-2/B |
| Notched izod impact (23°C) | 6 | kJ/m² | ISO 180/1A |
| Temp. of deflection under load (0,45 MPa) | 215 | °C | ISO 75-2/B |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Properties | 400 | V | EN 60112 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Properties | HB | EN 60695-11-10 |