EPLAMID 6 IMP NC Q1B001
- Chemical Family
- Polyamides
Unreinforced and modified polyamide 6 improved with good-impact resistance, heat stabilized and lubricated for injection molding.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- EPLAMID
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 1750.0 - 1750.0 MPa
- Processing Methods
- Injection Molding
- Notes
Eplamid 6 Impact modified compounds are used in all sectors of industry, offering a good impact strength for mechanical properties and ensures an outstanding performance even at low temperatures (up to -40°C).This material is available in natural and colors on request
- Markets
- Industrial
- Technology
- Plastics
- Material Features
- Good Impact Strength
- Heat Stabilized
- Impact Modified
- Impact Resistance
- Lubricated
- Plastics and Elastomers End Uses
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Unnotched izod impact (23°C) | No break | kJ/m² | ISO 180/1U |
| Flexural modulus (2mm/min) (23°C) | 1750 | MPa | ISO 178 |
| Flexural strength (2mm/min) (23°C) | 75 | MPa | ISO 178 |
| Tensile modulus (1mm/min) (23°C) | 2100 | MPa | ISO 527-2 |
| Tensile strain at break (50mm/min) (23°C) | min. 50 | MPa | ISO 527-2 |
| Tensile stress at break (50mm/min) (23°C) | 50 | MPa | ISO 527-2 |
| Unnotched charpy impact (23°C) | No break | kJ/m² | ISO 179/1eU |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold shrinkage- parallel/normal (3mm) | 1,4/2 | % | ISO 294-4 |
| Density (23°C) | 1,08 | g/cm3 | ISO 1183 |
| Determination of water content | 0,1 | % | ISO 1183 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Notched izod impact (-40°C) | 16 | °C | ISO 3146 |
| Melting point | 220 | °C | ISO 75-2/A |
| Notched charpy impact (23°C) | 30 | kJ/m² | ISO 75-2/B |
| Notched charpy impact (-30°C) | 20 | °C | ISO 75-2/B |
| Notched izod impact (23°C) | 25 | kJ/m² | ISO 180/1A |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Properties | 600 | V | EN 60112 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Properties | HB | ASTM D257 |