EPLAMID 6 CBR 30 NC Q1D001
- Chemical Family
- Polyamides
Polyamide 6 reinforced with 30 % of glass spheres, heat stabilized and lubricated for injection molding.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- EPLAMID
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Ball
- Flexural Modulus
- 3200.0 - 3200.0 MPa
- Processing Methods
- Injection Molding
- Notes
Eplamid 6 glass sphere reinforced grades offer a good surface finish, low warpage and good dimensional stability which are used in many sectors of industry.This material is available in natural and colors on request
- Markets
- Industrial
- Technology
- Plastics
- Material Features
- Dimensional Stability
- Good Surface Finish
- Heat Stabilized
- Low Warpage
- Lubricated
- Plastics and Elastomers End Uses
- Industrial Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Unnotched izod impact (23°C) | 35 | kJ/m² | ISO 180/1U |
| Flexural modulus (2mm/min) (23°C) | 3200 | MPa | ISO 178 |
| Flexural strength (2mm/min) (23°C) | 110 | MPa | ISO 178 |
| Tensile modulus (1mm/min) (23°C) | 4400 | MPa | ISO 527-2 |
| Tensile strain at break (5mm/min) (23°C) | 4 | MPa | ISO 527-2 |
| Tensile stress at break (5mm/min) (23°C) | 75 | MPa | ISO 527-2 |
| Unnotched charpy impact (23°C) | 50 | kJ/m² | ISO 179/1eU |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold shrinkage- parallel/normal (3mm) | 0,6/1,0 | % | ISO 294-4 |
| Ash content | 30 | % | ISO 3451-4 |
| Density (23°C) | 1,33 | g/cm3 | ISO 1183 |
| Determination of water content | 0,2 | % | ISO 1183 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temp. of deflection under load (1,80 MPa) | 70 | °C | ISO 75-2/A |
| Melting point | 220 | °C | ISO 3146 |
| Notched charpy impact (23°C) | 5 | kJ/m² | ISO 75-2/B |
| Notched izod impact (23°C) | 4 | kJ/m² | ISO 180/1A |
| Temp. of deflection under load (0,45 MPa) | 180 | °C | ISO 75-2/B |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Properties | 550 | V | EN 60112 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Properties | HB | EN 60695-11-10 |