EPLAMID HT02 GFR 50 NC Q1F001
- Chemical Family
- Polyamides
Partially Aromatic copolyamide with a combination of semi-crystalline polyamide reinforced with 50% Glass fiber, heat stabilized and lubricated for injection molding process.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Tooling & Moldmaking
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- EPLAMID
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Notes
Eplamid HT02 grades offer the following unique properties in general conditions, and even after moisture absorption: Good Surface Finish, Good Dimensional Stability, Good High Temperature Properties, Good Chemical Resistance to Glycols and Oils and Excellent Creep Resistance. Eplamid HT02 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required.This material is available in natural and colors on request
- Markets
- Industrial
- Technology
- Plastics
- Material Features
- Creep Resistant
- Dimensional Stability
- Good Surface Finish
- Heat Stabilized
- Lubricated
- Semi Crystalline
- Chemical Resistance
- Glycol
- Plastics and Elastomers End Uses
- Mold Making
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile modulus (1mm/min) (23°C) | 17500 | MPa | ISO 527-2 |
| Tensile strain at break (5mm/min) (23°C) | 2,5 | MPa | ISO 527-2 |
| Tensile stress at break (5mm/min) (23°C) | 235 | MPa | ISO 527-2 |
| Unnotched charpy impact (23°C) | 90 | kJ/m² | ISO 179/1eU |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ash content | 50 | % | ISO 3451-4 |
| Density (23°C) | 1,61 | g/cm3 | ISO 1183 |
| Determination of water content | 0,1 | % | ISO 1183 |
| Mold shrinkage- parallel/normal (3mm) | 0,1/0,6 | % | ISO 294-4 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Maximum working temp. long term | 140 | °C | ISO 3146 |
| Maximum working temp. short term | 250 | °C | ISO 3146 |
| Melting point | 310 | °C | ISO 75-2/A |
| Notched charpy impact (23°C) | 12 | kJ/m² | ISO 75-2/B |
| Notched charpy impact (-30°C) | 11 | °C | ISO 75-2/B |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Properties | 600 | V | EN 60112 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Properties | HB | ASTM D257 |