Wynca XHG-6310
- Chemical Family
- Silicones
Wynca XHG-6310 is a two-component liquid silicone rubber for injection molding or casting processes. It can be handled with high efficiency, no flash and low energy requirement. The rubber articles made with XHG-6310 is of high physical properties, high durability and good dielectric property.
Product families
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
- Consumer Electronics
- Switches & Relays
Product Families
- Silicone Elastomers
Other characteristics
- Features
Excellent Dielectric Properties, High Efficiency, Long Seal Life, Low Energy Consumption
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- PACKAGING
20kg PE lined plastic pails or 200kg PE lined metal drums.
- Appearance
- Translucent
- Usage
A static metering and mixing unit is recommended to feed the mixture of part A and part B in the ratio 1:1 to the injection molding machine. If air bubbles are entrapped during mixing, the mixture must be thoroughly degassed under vacuum. The standard curing temperature is 120-150℃ and the curing time also depends on the thickness of rubber products
- Processing
Please exactly control the mixing ratio of part A and part B, otherwise curing process and product properties may be affected.; The curing time, which depends on curing temperature and the thickness of rubber products, should be adjusted to meet the production needs.; Please strictly avoid the contact with certain materials such as amines, sulfur, phosphor and tin, which will adversely affect the curing process or even result in no curing.
- Technology
- Elastomers
- Packaging Type
- Drums
- Material Features
- Excellent Dielectric Properties
- High Efficiency
- Long Seal Life
- Low Energy Consumption
- Typical Applications
- Keypad
- Elastomeric switch
- Common rubber articles
- Storage and Transportation
Keep in cool and well ventilated place from rain, moisture and sunlight. When stored in the original unopened containers, this product has a shelf life of 6 months from the date of manufacture. The containers should be sealed tightly after use.. This product can be shipped as non-hazardous goods. Avoid fall, upside down and collision with hard objects during transportation.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids Content | 100 | % |
| Viscosity | 100 | Pa.s |
| Hardness (2mm thickness slabs molded 8 minutes at 150°C) | 40 | shore A |
| Tensile Strength (2mm thickness slabs molded 8 minutes at 150°C) | 4.5 | mPa |
| Tear Strength (2mm thickness slabs molded 8 minutes at 150°C) | 11 | kN/m |
| Elongation (2mm thickness slabs molded 8 minutes at 150°C) | 200 | % |
Table 2 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Strength (1mm thickness slabs molded 8 minutes at 150°C) | 18 | kV/mm |
| Volume Resistivity (1mm thickness slabs molded 8 minutes at 150°C) | 10^14 | Ohm.cm |
Table 3 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| T10 5 minutes at 150°C | 10 | s |
| T90 5 minutes at 150°C | 30 | s |