Wynca XHG-6330
- Chemical Family
- Silicones
Wynca XHG-6330 is a two-component, low viscosity liquid silicone rubber designed for electric and electronic potting. It is flame retardant and provides good dielectric property and excellent resistance to temperature extremes.
Product families
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications
- Powertrain & UTH
- Connectors
- Sensors & Actuators
- Power & Utilities
Product Families
- Silicone Elastomers
Other characteristics
- End Uses
- Electrical/Electronic Applications
- Features
Excellent Dielectric Properties, Flame Resistant, High Temperature Resistance, Long Seal Life, Low Viscosity
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- PACKAGING
- 20kg metal pails.
- Appearance
- Off-white
- Usage
To ensure uniform distribution of the filler in the material, both part A and part B should be thorough mixed separately before mixing part A and part B in the ratio of 1:1. If air bubbles are entrapped during mixing, the mixture must be thoroughly degassed under vacuum. This material can be either heat cured or cured at room temperature. The curing time depends on the thickness of potting and can be adjusted from one hour to dozens of hours to meet different needs.
- Processing
Please exactly control the mixing ratio of part A and part B, otherwise curing process and product properties may be affected.; The curing time, which depends on curing temperature and the thickness of potting, should be adjusted to meet the production needs.; Please strictly avoid the contact with certain materials such as amines, sulfur, phosphor and tin, which will adversely affect the curing process or even result in no curing.
- Technology
- Elastomers
- Packaging Type
- Pails
- Material Features
- Excellent Dielectric Properties
- Flame Resistant
- High Temperature Resistance
- Long Seal Life
- Low Viscosity
- Typical Applications
Potting of electronic assemblies such as power unit, connectors and sensors.. Potting of electric controller, transformer, power amplifier, high voltage resistor and contact modules
- Storage and Transportation
Keep in cool and well ventilated place from rain, moisture and sunlight. When stored in the original unopened containers, this product has a shelf life of 6 months from the date of manufacture. The containers should be sealed tightly after use.. This product can be shipped as non-hazardous goods. Avoid fall, upside down and collision with hard objects during transportation.
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids Content | 100 | % |
| Viscosity (A) | 4.5 | Pa.s |
| Viscosity (B) | 1.5 | Pa.s |
| Hardness (2mm thickness slabs molded 8 minutes at 150°C) | 40 | shore A |
| Tensile Strength (2mm thickness slabs molded 8 minutes at 150°C) | 2.4 | mPa |
| Tear Strength (2mm thickness slabs molded 8 minutes at 150°C) | 5 | kN/m |
| Elongation (2mm thickness slabs molded 8 minutes at 150°C) | 140 | % |
Table 2 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Thermal Conductivity | 0.55 | w/m.K |
| Thermal Expansion Co-efficient (1/k) | 2.6x10-4 | — |
| Flammability Classification | 94V-0 | — |
Table 3 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Strength (1mm thickness slabs molded 8 minutes at 150°C) | 22 | kV/mm |
| Volume Resistivity (1mm thickness slabs molded 8 minutes at 150°C) | 5x10^14 | Ohm.cm |
| Dissipation Factor (1mm thickness slabs molded 8 minutes at 150°C) | 0.01 | — |
| Tracking Resistance (1mm thickness slabs molded 8 minutes at 150°C) | 3.1 | — |