HOMOPOLYMER POLYPROPYLENE (PP) FY3011E
- Chemical Family
- PolyolefinsPolypropylenes (PP)
HOMOPOLYMER POLYPROPYLENE (PP) FY3011E is a polypropylene homopolymer intended for yarn extrusion characterized by ease of processing and low heat shrinkage. Yarn made from this resin exhibit excellent mechanical property.
Product families
Applications
Applications
- Consumer Goods — Carpet & Upholstery
Industrial — Leather & Textiles
- Textile Manufacturing
Printing & Packaging — Packaging
- Food & Beverage Packaging
Adhesives & Sealants — Packaging & Paper
- Tape & Label Adhesives
Printing & Packaging — Tapes, Labels & Adhesives
- Tapes & Labels
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- HOMOPOLYMER POLYPROPYLENE (PP)
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Processing Methods
- Extrusion
- Markets
- Adhesives & Sealants
- Consumer Goods
- Industrial
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Good Mechanical Properties
- Homopolymer
- Low Shrinkage
- Storage and Handling
FY3011E should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperature below 50 ºC. It is advisable to process polypropylene resins within 6 months after delivery.
- Processing Conditions
- Recommended Extrusion Temperature
- 230 – 260 ºC
- Stretching Temperature
- 140 – 160 ºC
- Stretching Ratio 4-6.
- Plastics and Elastomers End Uses
- Tape
- Wovens Coatings
- Yarn
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 34 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 9 | % | ASTM D638 |
| Tensile Strength at Break | 19 | MPa | ASTM D638 |
| Tensile Elongation at Break | 165 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Flexural Strength | 35 | MPa | ASTM D790 |
| Izod Impact, Notched 23ºC | 3 | kJ/m2 | ASTM D256 |
| Rockwell Hardness | 98 | — | ASTM D785 |
Table 2 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature at 10N | 152 | ºC | ASTM D1525 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFR (230ºC/2.16Kg) | 3 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D792 Method A |