HOMOPOLYMER POLYPROPYLENE (PP) FS3011E

Chemical Family: PolyolefinsPolypropylenes (PP)

HOMOPOLYMER POLYPROPYLENE (PP) FS3011E is a polypropylene homopolymer intended for the extrusion of biaxially oriented film. It is easy to process and suitable for high speed BOPP line. The film made from this resin exhibits excellent transparency, excellent mechanical and barrier properties. It is also suitable for metallization.

Product families

Applications

Building & Construction — Decorative Materials & Finishes

Wallcoverings & Decorative Laminates

Printing & Packaging — Packaging

Food & Beverage Packaging

Adhesives & Sealants — Packaging & Paper

Tape & Label Adhesives

Printing & Packaging — Printing & Inks

Other Printing Applications

Printing & Packaging — Tapes, Labels & Adhesives

Tapes & Labels

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand

HOMOPOLYMER POLYPROPYLENE (PP)

Polymer Name

Polypropylene Homopolymer (HPP)

Processing Methods

Extrusion, Lamination

Markets

Adhesives & Sealants
Building & Construction
Printing & Packaging

Technology

Plastics

Material Features

Excellent Transparency Properties
Good Barrier Properties
Good Mechanical Properties
Homopolymer

Storage and Handling

FS3011E should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperature below 50 ºC. It is advisable to process polypropylene resins within 6 months after delivery.

Processing Conditions

Recommended Extrusion Temperature: 190 – 250 ºC
Stretching Temperature: 130 – 160 ºC
Stretching Ratio MD/TD: 4-7 / 7-10.

Plastics and Elastomers End Uses

Biaxially Oriented Film
Film
Oriented Film
Tape

Plastics and Elastomers Functions

Resin

Plastics and Elastomers Processing Methods

Extrusion
Lamination

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Strength at Yield	32	MPa	ASTM D638
Tensile Elongation at Yield	9	%	ASTM D638
Tensile Strength at Break	19	MPa	ASTM D638
Tensile Elongation at Break	165	%	ASTM D638
Flexural Modulus	1265	MPa	ASTM D790
Flexural Strength	35	MPa	ASTM D790
Izod Impact, Notched 23ºC	2.8	kJ/m2	ASTM D256
Rockwell Hardness	98	—	ASTM D785

Table 2 of 4

1 row

Characteristic	Value	Unit	Method
Vicat Softening Temperature at 10N	153	ºC	ASTM D1525