ASTC 1007 Polyurea Spray

Other characteristics

Features

Abrasion Resistant, Chemical Resistant, Good Bonding Strength, High Elongation, High Hydrolytic Stability, High Performance, High Tensile Strength, Impact Resistance, Low Permeability, Skid Resistant

Product Type

2K (2 component) Coating, Solventless & High Solids Coating

Application Method

Spray

Compatible Substrates & Surfaces

Concrete, Metal, Wood

Color

Black, Dark Gray, Tan

Note

The best spray application results are obtained coating concrete when the ambient temperature is decreasing. In applications where it is not possible to use the temperature to your advantage it is suggested that the ASTC's CMW be used in conjunction with PenPrime and the polyurea coating.

Prime

Prime ith ASTC primer PenPrime. Prime 2-4 hours prior to the 1007 application for best results. Spray the polyurea on the primer only after the primer has become tack free.

Finish

The finish of this product is best using a stipple surface with the 1007 over freshly applied 1007.

Safety

This product is for use by professional applicators only. Wear Protective Clothing and gloves as the product bonds very well to fabrics. Read MSDS before using this product. DOT/Flash Point Non-flammable Liquid Classification, not regulated.

Markets

• Automotive & Transportation
• Building & Construction
• Paints & Coatings

Potlife

none .

Priming

1007 cross-links with the ASTC primer PenPrime and produces excellent results when used together as a system.

PACKAGING

110 gallon kits

Application Area

• Secondary containment with non-skid
• Corrosive barrier, protective coating protection
• Processing equipment
• Concrete tanks &steel tanks
• Secondary containment walls and floors
• All industrial service surfaces
• Geotextile containment appucations

Advantages

Excellent elongation-400%+; Excellent for containment, refineries, chemical; Plants, marine applications and other industrial; Faciluties; Designed to chemically bond to astc primers; Protects concrete and other surfaces, wood, metal, etc.; Chemical resistant; High impact & abrasion resistance

Components

Two part system; 1:1 ratio

Application

Use only heated high pressure equipment & impingement gun equipment, fluid pressure of 2,000 psi. Minimum heat 160F. Surface temperature -209F to 120 F. Apply at not less than 59F above dew point. Apply at specified mil thickness over primer as required for the application. Spraying 1007 requires special equipment, user must be a professional applicator qualified in the use of high performance polyurea materials and specialty application equipment.

Show in full

Dry Time

As soon as the sprayed surface will allow access not more then 1-1.5 hours after first application. Full cure in 24 to 48@70°F

Limitations

Do not use on wet surfaces or expose part A to moisture. Keep out of direct sunlight, store drum kits on wood pallets at room temperature. Always mix the part B before using, continue agitation of Part B during application. Pre- heat drums as needed per environmental temperature. Best results over vapor barrier and/or compatible primer.

Show in full

Preparation

Concrete must have a minimum 28 day cure prior to application. Remove any curing agent, form release materials, oils, wax, moisture or any material that may affect bonding. Clean and wash to remove contaminants and maintain pH 8.0-11.0. Perform a Moisture Vapor Test before making the coating application on concrete. Provide rough surface profile minimum 2-3 mils. Seal/repair all bug-holes, cracks and spalls, see ASTC data sheets on 830, 4034 and 3004 joints).

Show in full