XECARB® HM 29-C30
- Chemical Family
- Polyamides
XECARB® HM 29-C30 is a 30% carbon fiber reinforced PA4.10
Product families
Applications
Applications
- Consumer Goods — Footwear
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Composite Materials — Polymers & Resins
- Thermoplastic Resins
Other characteristics
- Brand
- XECARB® HM
- Polymer Name
- Polyamide 410 (PA 410)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Reinforcement Material
- Carbon Fibers
- Markets
- Consumer Goods
- Industrial
- Technology
- Composite Materials
- Plastics
- Material Features
- Excellent Tensile Properties
- Good Tenacity
- High Stiffness
- High Tensile Strength
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Plastics and Elastomers End Uses
- Industrial Applications
- Mountaineering Boots
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dam) | 1.23 | g/cm3 | ISO 1183 |
Table 2 of 3
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min, Dam) | 25900.0 | MPa | ISO 527 |
| Tensile Strength (at Break, 5 mm/min, Dam) | 280.0 | MPa | ISO 527 |
| Tensile Elongation (at Break, 5 mm/min, Dam) | 2.1 | % | ISO 527 |
| Flexural Modulus (at 2 mm/min, Dam) | 20300.0 | MPa | ISO 178 |
| Flexural Strength (at 2 mm/min, Dam) | 400.0 | MPa | ISO 178 |
| Flexural Strain (at Break, 2 mm/min, Dam) | 2.8 | % | ISO 178 |
| Notched Izod Impact Strength (at 23°C, 50% RH, Dam) | 12.0 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at 23°C, 50% RH, Dam) | 73.0 | kJ/m2 | ISO 180 |
| Notched Izod Impact Strength (at -30°C, Dam) | 9.0 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at -30°C, Dam) | 66.0 | kJ/m2 | ISO 180 |
Table 3 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | Desiccant Dryer |
| Drying Time | 6 - 8 | hrs | Desiccant Dryer |
| Melt Temperature | 265 - 275 | °C | — |
| Mould Temperature | 95.0 | °C | — |