XEGLASS™ 17-G50-P3
- Chemical Family
- Polyamides
XEGLASS™ 17-G50-P3 is a 50% glass fiber reinforced PEBA
Product families
Applications
- Consumer Goods — Sports & Recreation
- Equipment & Parts
Product Families
- Thermoplastic Polyamide Elastomers (TPE-A)
Other characteristics
- Brand
- XEGLASS
- End Uses
- Gears, Industrial Applications, Structural Parts
- Features
Chemical Resistant, Creep Resistant, Dimensional Stability, Easier Processing, Flexible, Good Impact Strength, Good Mechanical Properties, Good Stiffness, High Impact Resistance, Low Density, Low Friction, Low Temperature Impact Resistance, Noise Damping, Pigmentable, Superior Aesthetics, Vibration Damping
- Polymer Name
- Polyether Block Amide (PEBA)
- Flexural Modulus
- 7000.0 - 7000.0 MPa
- Markets
- Consumer Goods
- Industrial
- Technology
- Elastomers
- Labeling Claims
- Plasticizer-free
- Processing Note
Under the recommended processing condition small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
- Fillers Included
- Glass Fiber
- Material Features
- Chemical Resistant
- Creep Resistant
- Dimensional Stability
- Easier Processing
- Flexible
- Good Impact Strength
- Good Mechanical Properties
- Good Stiffness
- Plastics and Elastomers End Uses
- Gears
- Industrial Applications
- Structural Parts
Technical data
Table 1 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dam) | 1.45 | g/cm3 | ISO 1183 |
| Post Shrinkage (Parallel, Dam) | 0.35 | % | Sim.ISO 294-4 |
| Post Shrinkage (Normal, Dam) | 0.45 | % | Sim.ISO 294-4 |
Table 2 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min, Dam) | 8000 | MPa | ISO 527 |
| Tensile Strength (at Break, 5 mm/min, Dam) | 115 | MPa | ISO 527 |
| Tensile Elongation (at Break, 5 mm/min, Dam) | 6 | % | ISO 527 |
| Flexural Modulus (at 2 mm/min, Dam) | 7000 | MPa | ISO 178 |
| Flexural Stress (at 3.5% Strain, 2 mm/min, Dam) | 145 | MPa | ISO 178 |
| Notched Izod Impact Strength (at 23°C, 50% RH, Dam) | 31 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at 23°C, 50% RH, Dam) | 93 | kJ/m2 | ISO 180 |
| Notched Izod Impact Strength (at -30°C, Dam) | 21 | kJ/m2 | ISO 180 |
| Unnotched Izod Impact Strength (at -30°C, Dam) | 81 | kJ/m2 | ISO 180 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 8 MPa, 120°C/h, Dam) | 105 | °C | ISO 75 |
| Vicat Softening Temperature (at 50 N, 120°C/h, Dam) | 160 | °C | ISO 306 |
Table 4 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | Desiccant Dryer |
| Drying Time | 6 - 8 | hrs | Desiccant Dryer |
| Mould Temperature | 35 | °C | — |
| Melt Temperature | 240 - 255 | °C | — |