XEBRID™ 1-C10-G40

Chemical Family: Polyamides

XEBRID™ 1-C10-G40 is a 10% carbon fiber + 40% glass fiber reinforced PA66

Product families

Applications

Consumer Goods — Footwear

Personal Care — Packaging & Accessories

Applicators & Accessories

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Composite Materials — Polymers & Resins

Thermoplastic Resins

Other characteristics

Brand: XEBRID
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Carbon Fiber, Glass Fiber
Carbon Fiber
Glass Fiber
Processing Methods: Injection Molding
Reinforcement Material: Carbon Fibers, Glass Fibers
Carbon Fibers
Glass Fibers
Markets: Consumer Goods
Personal Care
Technology: Composite Materials
Plastics
Processing Note: Under the recommended processing condition small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Material Features: Anti-Static
Cost Effective
Enhanced Physical Properties
Good Mechanical Properties
Good Processability
Good Stiffness
Light Weight
Composite Materials Functions: Resins Binders & Matrix Materials
Plastics and Elastomers End Uses: Hair Combs
Hair Curler Brushes
Mountaineering Boots
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

3 rows

Characteristic	Value	Unit	Method
Density (Dam)	1.52	g/cm3	ISO 1183
Post Shrinkage (Parallel, Dam)	0.25	%	Sim.ISO 294-4
Post Shrinkage (Normal, Dam)	0.3	%	Sim.ISO 294-4

Table 2 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Modulus (at 1 mm/min, Dam)	20500	MPa	ISO 527
Tensile Strength (at Break, 5 mm/min, Dam)	230	MPa	ISO 527
Tensile Elongation (at Break, 5 mm/min, Dam)	2.1	%	ISO 527
Flexural Modulus (at 2 mm/min, Dam)	15200	MPa	ISO 178
Flexural Strength (at 2 mm/min, Dam)	310	MPa	ISO 178
Flexural Strain (at Break, 2 mm/min, Dam)	2.6	%	ISO 178
Notched Izod Impact Strength (at 23°C, 50% RH, Dam)	11	kJ/m2	ISO 180
Unnotched Izod Impact Strength (at 23°C, 50% RH, Dam)	68	kJ/m2	ISO 180
Notched Izod Impact Strength (at -30°C, Dam)	10	kJ/m2	ISO 180
Unnotched Izod Impact Strength (at -30°C, Dam)	66	kJ/m2	ISO 180

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 8 MPa, 120°C/h, Dam)	195	°C	ISO 75
Vicat Softening Temperature (at 50 N, 120°C/h, Dam)	240	°C	ISO 306

Table 4 of 5