Exolon® Vista QX
- Chemical Family
- Polycarbonate (PC)
Exolon® Vista QX sheets are clear, polished polycarbonate sheets with enhanced optical properties. They offer extreme impact strength that exceeds the physical properties of other products of their class. Exolon® Vista QX sheets resist temperatures of -100 to +120 °C, exhibit high optical clarity and have good fire properties. The sheets offer protection against involuntary breakage and willful destruction. Exolon® Vista QX sheets can be thermoformed, cold-curved and machined with ease.
Properties
- Physical Form
- Sheets
Product families
- Exterior & Body
Other characteristics
- Brand
- Exolon
- Color
- Transparent
- Density
- 1200.0 - 1200.0 kg/m³
- Features
Good Impact Strength, Good Optical Properties, Improved Optical Clarity, Light Weight, Temperature Resistance
- Polymer Name
- Polycarbonate (PC)
- Tensile Modulus
- 2350.0 - 2350.0 MPa
- Markets
- Automotive & Transportation
- Benefits
- Enhanced Optical Quality
- Extreme Impact Strength
- Resistance To A Wide Range Of Temperatures
- Technology
- Plastics
- Available Sizes
Exolon® Vista QX7 and QX90 are available in thicknesses of 3 - 12 mm and Exolon® Vista QX10 and QX200 in thicknesses of 3 - 8 mm.. Sizes (standard) : 3,050 x 2,050 mm
- Product Families
- Plastics — Parts, Shapes & Films
- Composites End Use
- Profiles
- Material Features
- Good Impact Strength
- Good Optical Properties
- Improved Optical Clarity
- Light Weight
- Temperature Resistance
- Plastics and Elastomers End Uses
- Door Profiles
- Glazing
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength (23°C, 3 mm, Notched) | 80P | kg/m² | ISO 179-1eA |
| Charpy Impact Strength (23°C, Unnotched) | non-break | kg/m² | ISO 179-1eU |
| Flexural Modulus (2 mm/min) | 2350.0 | MPa | ISO 178 |
| Flexural Strength (2 mm/min) | min. 90 | MPa | ISO 178 |
| Izod Impact Strength (23°C, 3.2 mm, Notched) | 70P | kg/m² | ISO 180-A |
| Nominal Strain at Break (50 mm/min) | min. 50 | % | ISO 527-1,-2 |
| Tensile Modulus (1 mm/min) | 2350.0 | MPa | ISO 527-1,-2 |
| Yield Strain (50 mm/min) | 6.0 | % | ISO 527-1,-2 |
| Yield Stress (50 mm/min) | min. 60 | MPa | ISO 527-1,-2 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183-1 |
| Refractive Index (Procedure A) | 1.587 | — | ISO 489 |
| Water Absorption Equilibrium (23°C, 50% Relative Humidity) | 0.12 | % | ISO 62 |
| Water Absorption Saturation (23°C) | 0.3 | % | ISO 62 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 0.65 | 10⁻⁴/K | ISO 11359-1 |
| Temperature of Deflection Under Load (0.45 Mpa) | 140.0 | °C | ISO 75-1, -2 |
| Temperature of Deflection Under Load (1.80 Mpa) | 128.0 | °C | ISO 75-1, -2 |
| Thermal Conductivity (23°C) | 0.2 | W/mK | ISO 8302 |
| Vicat Softening Temperature (50 N, 50°C/h) | 148.0 | °C | ISO 306 |
Table 4 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Permanent Service Temperature (Without Load) | approx. 120 | °C |
Table 5 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dissipation Factor (1 Mhz) | 95.0 | 10⁻⁴ | IEC 60250 |
| Dissipation Factor (100 Hz) | 5.0 | 10⁻⁴ | IEC 60250 |
| Electrical Strength (1 mm) | 34.0 | kV/mm | IEC 60243-1 |
| Relative Permitivity (1 Mhz) | 3.0 | — | IEC 60250 |
| Relative Permitivity (100 Hz) | 3.1 | — | IEC 60250 |
| Surface Resistivity | 1e¹⁶ | Ohm | IEC 60093 |
| Volume Resistivity | 1e¹⁴ | Ohm.m | IEC 60093 |