Exolon® AR
- Chemical Family
- Polycarbonate (PC)
Exolon® AR sheet is an abrasion and enhanced UV resistant polycarbonate sheet that offers glasslike hardness coupled with the impact strength of standard polycarbonate. Exolon® AR has a 10-years warranty against breakage and 7-years warranty against delamination and weathering.
Properties
- Physical Form
- Sheets
Product families
Building & Construction — Building Envelope & Roofing
- EIFS & Insulation
- Glazing & Window Elements
Other characteristics
- Brand
- Exolon
- Color
- Bronze, Transparent
- Bronze
- Transparent
- Density
- 1200.0 - 1200.0 kg/m³
- Features
Abrasion Resistant, Good Impact Strength, Good Non-Yellowing Properties, Good Weather Stability, High Clarity, Long Shelf Life, Low Haze, UV Resistant
- Polymer Name
- Polycarbonate (PC)
- Tensile Modulus
- 2350.0 - 2350.0 MPa
- Markets
- Building & Construction
- Benefits
- Extreme Impact Strength
- Good Abrasion Resistance
- Excellent Weathering Resistance
- High Clarity
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Available Sizes
Exolon® AR is available in thicknesses of 3 – 15 mm and in the following sizes :
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Abrasion Resistant
- Good Impact Strength
- Good Non-Yellowing Properties
- Good Weather Stability
- High Clarity
- Long Shelf Life
- Low Haze
- UV Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Acoustic Barrier
- Glazing
Technical data
Table 1 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength (23°C, 3 mm, Notched) | 80P | kg/m² | ISO 179-1eA |
| Charpy Impact Strength (23°C, Unnotched) | non-break | kg/m² | ISO 179-1eU |
| Flexural Modulus (2 mm/min) | 2350.0 | MPa | ISO 178 |
| Flexural Strength (2 mm/min) | 90.0 | MPa | ISO 178 |
| Izod Impact Strength (23°C, 3.2 mm, Notched) | 70P | kg/m² | ISO 180-A |
| Nominal Strain at Break (50 mm/min) | min. 50 | % | ISO 527-1,-2 |
| Taber Abrasion Resistance (Δ Haze After 100 Cycles, 500 G Cs 10F) | 1 - 4 | % | ASTM D1044 |
| Taber Abrasion Resistance (Δ Haze After 500 Cycles) | 4 - 9 | % | ANSI Z26.1 |
| Tensile Modulus (1 mm/min) | 2350.0 | MPa | ISO 527-1,-2 |
| Yield Strain (50 mm/min) | 6.0 | % | ISO 527-1,-2 |
| Yield Stress (50 mm/min) | min. 60 | MPa | ISO 527-1,-2 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183-1 |
| Refractive Index (Procedure A) | 1.587 | — | ISO 489 |
| Water Absorption Equilibrium (23°C, 50% Relative Humidity) | 0.12 | % | ISO 62 |
| Water Absorption Saturation (23°C) | 0.3 | % | ISO 62 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 0.65 | 10⁻⁴/K | ISO 11359-1 |
| Temperature of Deflection Under Load (0.45 Mpa) | 140.0 | °C | ISO 75-1, -2 |
| Temperature of Deflection Under Load (1.80 Mpa) | 128.0 | °C | ISO 75-1, -2 |
| Thermal Conductivity (23°C) | 0.2 | W/mK | ISO 8302 |
| Vicat Softening Temperature (50 N, 50°C/h) | 148.0 | °C | ISO 306 |
Table 4 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Permanent Service Temperature (Without Load) | approx. 120 | °C |