ULTRASIL® VN 3 GR
- Chemical Name
- Silica gel pptd. cryst.-free
- Chemical Family
- Silica
ULTRASIL® VN 3 GR has a specific N2 surface area of approximately 180m²/g and is utilized in nearly all areas of the rubber industry. It is available in both powdered and granulated forms. ULTRASIL® VN 3 GR offers a high reinforcing potential in combination with a high level of transparency in the finished rubber product, such as in shoe soles. Furthermore, ULTRASIL® VN 3 GR is widely used in different bonding systems.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
- Consumer Goods — Footwear
- Tires
- Equipment & Parts
Product Families
- Fillers & Extenders
Other characteristics
- Brand
- ULTRASIL
- Features
Dust-Free, Excellent Transparency Properties, Good Abrasion Resistance, Good Processability, High Dispersibility, High Hardness, High Tensile Strength, Tear Resistance
- Functions
- Reinforcement
- Note
1) based on original substance 2) based on ignited substance (2 h/1000°C) *) The given data are typical values. Specifications on request.
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Appearance
- White granule
- Shelf LIfe
- 2 years
- Technology
- Elastomers
- Labeling Claims
- Not Listed In California Proposition 65
- Material Features
- Dust-Free
- Excellent Transparency Properties
- Good Abrasion Resistance
- Good Processability
- High Dispersibility
- High Hardness
- High Tensile Strength
- Tear Resistance
- Chemical Description
SiO₂, synthetically produced amorphous silicon dioxide.
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ENCS (Japan)
- IECSC (China)
- KECI (Korea)
- NZIoC (New Zealand)
- PICCS (Phillipines)
- Applications
ULTRASIL VN 3 GR is a mechanically compacted granulate. On account of the granulation process it leads to less dust development during mixing. ULTRASIL VN 3 GR has a high reinforcing potential and imparts to rubber compounds high Shore hardness, tensile strength, tear resistance and abrasion resistance. In order to achieve optimum rubber-technical data the addition of activators like glycols, amines or other alkaline accelerators is necessary. On account of the higher surface area ULTRASIL VN 3 GR can provide vulcanizates of excellent transparency. Application fields are: Tires, mechanical rubber goods, cables and shoe soles of all kinds. ULTRASIL VN 3 GR as a precipitated silica is used as a reinforcing filler in all kind of rubber applications.
- Packaging Information
Our silica products are inert and extremely stable chemically. However, due to their high specific surface area, they can absorb moisture and volatile organic compounds from the surrounding atmosphere. Therefore, we recommend storing the products in sealed containers in a dry, cool place, and removed from volatile organic substances. Even if a product is stored under these conditions, after a longer period it can still pick up ambient moisture over time, which could lead to its exceeding the specified moisture content. For this reason, our recommended use-by date is 24 months after date of manufacture. Product more than 24 months old should be tested for moisture content before use in order to make certain that it is still suitable for the intended application.
- Certifications and Compliance
- REACH (Europe)
- Plastics and Elastomers End Uses
- Tires
- Plastics and Elastomers Functions
- Reinforcement
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Manganese Content¹ | max. 6 | ppm | Internal Method |
| Copper Content¹ | max. 6 | ppm | Internal Method |
| Iron Content¹ | max. 400 | ppm | Internal Method |
| SiO₂ Content² | min. 97 | % | ISO 3262-19 |
| SA Ro-Tap (< 75 µm) | max. 1300 | % | ISO 5794-1F |
| SA Ro-Tap (> 300 µm) | max. 10 | % | ISO 5794-1F |
| Electrical Conductivity (4% in water) | max. 1300 | µS/cm | ISO 787-14 |
| Pour Density | 280 | g/l | ASTM D1513 |
| pH Value (5 % in water) | 6.2 | — | ISO 787-9 |
| Loss on Drying (2h at 105°C) | 5.5 | % | ISO 787-2 |
| Specific Surface Area (CTAB) | 167 | m²/g | ISO 5794-1G |
| Specific Surface Area (N₂, Multipoint) | 180 | m²/g | ISO 9277 |