VESTAKEEP® 5000 CF30
- Chemical Family
- Polyether Ether Ketone (PEEK)
VESTAKEEP® 5000 CF30 is a Polyether Ether Ketone compound with a filler content of 30% carbon fibers and an ultra-high viscosity. It is primarily used for injection molding parts and is produced through a multistage process using hydroquinone and 4,4'-difluorobenzophenone building blocks.
Product families
Applications
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- VESTAKEEP
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Carbon Fiber
- Materials Features
Abrasion Resistant, Acid Resistant, Alkali Resistant, Chemical Resistant, Dimensional Stability, Electrically Insulating, Gasoline Resistant, Good Mechanical Properties, High Dielectric Strength, High Pressure Applications, High Stiffness, High Strength, High Temperature Application, High Viscosity, Hydraulic Fluid Resistant, Hydrocarbon Resistant, Oil Resistant, Salt Water/Spray Resistant, Seawater Resistant, Solvent Resistant, Water Resistant, Wear Resistant
- Processing Methods
- Extrusion, Injection Molding, Isostatic Molding
- Markets
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 V0
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Acid Resistant
- Alkali Resistant
- Chemical Resistant
- Dimensional Stability
- Electrically Insulating
- Gasoline Resistant
- Good Mechanical Properties
- Certifications and Compliance
- ISO 14001
- ISO 9001
- Plastics and Elastomers End Uses
- Compressor Components
- Electrical Connectors
- Packing Rings
- Seals
- Switches
- Valve Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
- Isostatic Molding
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (23°C) | 1.4 | g/cm³ | ISO 1183 |
| Melting Range DSC (2nd Heating) | approx. 340 | °C | ISO 11357 |
| Temperature of Deflection Under Load Method A (1.8 Mpa) | 324 | °C | ISO 75-1 |
| Temperature of Deflection Under Load Method B (0.45 Mpa) | 338 | °C | ISO 75-2 |
| Vicat Softening Temperature Method A (10 N) | 341 | °C | ISO 306 |
| Vicat Softening Temperature Method B (50 N) | 339 | °C | ISO 306 |
| Tensile Test - Tensile Strength (5 mm / min) | 230 | MPa | ISO 527-1/-2 |
| Tensile Test - Strain at Break (5 mm / min) | 2 | % | ISO 527-1/-2 |
| Tensile Modulus | 22500 | MPa | ISO 527-1/-2 |
| Charpy Impact Strength (23°C) | 59C | kJ/cm² | ISO 179/1eU |
| Charpy Notched Impact Strength (23°C) | 12C | kJ/cm² | ISO 179/1eA |