Exolon® UV
- Chemical Family
- Polycarbonate (PC)
Exolon® UV sheets are made from clear-transparent polycarbonate sheets with UV protection on both sides. They are the perfect choice for a long service life owing to their good weathering resistance. These attributes are backed up by a 10 year guarantee on weathering resistance and a 10 year guarantee on retaining their mechanical properties.
Properties
- Physical Form
- Sheets
Product families
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
- Waterproofing & Weatherproofing
Other characteristics
- Brand
- Exolon
- Color
- Blue, Bronze, Green, Grey, Transparent, White
- Blue
- Bronze
- Green
- Grey
- Transparent
- White
- Density
- 1200.0 - 1200.0 kg/m³
- Features
Good Impact Strength, Good Mechanical Properties, Good UV Protection, Good Weather Stability, Long Shelf Life
- Polymer Name
- Polycarbonate (PC)
- Tensile Modulus
- 2350.0 - 2350.0 MPa
- Markets
- Building & Construction
- Benefits
- Excellent Weathering Resistance
- Extreme Impact Strength
- Good Fire Rating
- Thermoformable
- Technology
- Plastics
- Available Sizes
Exolon® UV is available in thicknesses of 2 – 15 mm and in the following sizes :; Colors :; Clear 2099; White 2130; White 2150; Bronze 2850; Gray 2760; Blue 2550; Green 2650; Sizes (Standard) :; 3,050 x 2,050 mm; 6,110 x 2,050 mm
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Good Impact Strength
- Good Mechanical Properties
- Good UV Protection
- Good Weather Stability
- Long Shelf Life
- Plastics and Elastomers End Uses
- Roofing Elements
- Plastics and Elastomers Processing Methods
- Thermoforming
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength (23°C, 3 mm, Notched) | 80P | kg/m² | ISO 179-1eA |
| Charpy Impact Strength (23°C, Unnotched) | non-break | kg/m² | ISO 179-1eU |
| Flexural Modulus (2 mm/min) | 2350.0 | MPa | ISO 178 |
| Flexural Strength (2 mm/min) | 90.0 | MPa | ISO 178 |
| Izod Impact Strength (23°C, 3.2 mm, Notched) | 70P | kg/m² | ISO 180-A |
| Nominal Strain at Break (50 mm/min) | min. 50 | % | ISO 527-1,-2 |
| Tensile Modulus (1 mm/min) | 2350.0 | MPa | ISO 527-1,-2 |
| Yield Strain (50 mm/min) | 6.0 | % | ISO 527-1,-2 |
| Yield Stress (50 mm/min) | min. 60 | MPa | ISO 527-1,-2 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183-1 |
| Refractive Index (Procedure A) | 1.587 | — | ISO 489 |
| Water Absorption Equilibrium (23°C, 50% Relative Humidity) | 0.12 | % | ISO 62 |
| Water Absorption Saturation (23°C) | 0.3 | % | ISO 62 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 0.65 | 10⁻⁴/K | ISO 11359-1 |
| Temperature of Deflection Under Load (0.45 Mpa) | 140.0 | °C | ISO 75-1, -2 |
| Temperature of Deflection Under Load (1.80 Mpa) | 128.0 | °C | ISO 75-1, -2 |
| Thermal Conductivity (23°C) | 0.2 | W/mK | ISO 8302 |
| Vicat Softening Temperature (50 N, 50°C/h) | 148.0 | °C | ISO 306 |
Table 4 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Permanent Service Temperature (Without Load) | approx. 120 | °C |
Table 5 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dissipation Factor (1 Mhz) | 95.0 | 10⁻⁴ | IEC 60250 |
| Dissipation Factor (100 Hz) | 5.0 | 10⁻⁴ | IEC 60250 |
| Electrical Strength (1 mm) | 34.0 | kV/mm | IEC 60243-1 |
| Relative Permitivity (1 Mhz) | 3.0 | — | IEC 60250 |
| Relative Permitivity (100 Hz) | 3.1 | — | IEC 60250 |
| Surface Resistivity | 1e¹⁶ | Ohm | IEC 60093 |
| Volume Resistivity | 1e¹⁴ | Ohm.m | IEC 60093 |