Exolon® UV ClimateControl
- Chemical Family
- Polycarbonate (PC)
Exolon® UV ClimateControl is a transparent polycarbonate sheet with a protective UV coating on both sides. The sheets substantially reduce high temperatures caused by sunlight as they block out the majority of infrared light. It is extremely resistant to permanent environmental impacts and has a long service life. The maximum permissible temperature for long-term use in the absence of loads is in the region of 120°C. An additional benefit, is that the sheets come with a 10-year warranty on weather resistance, transparency and breaking strength.
Properties
- Physical Form
- Sheets
Product families
- Glazing & Window Elements
- Other Building Envelope & Roofing Applications
- Waterproofing & Weatherproofing
Other characteristics
- Brand
- Exolon
- Color
- Green, Transparent
- Green
- Transparent
- Density
- 1200.0 - 1200.0 kg/m³
- Features
Excellent Transparency Properties, Good Environmental Stress Crack Resistance (ESCR), Good Impact Strength, Good UV Protection, Good Weather Stability, Long Shelf Life, Sunlight Resistant
- Polymer Name
- Polycarbonate (PC)
- Tensile Modulus
- 2350.0 - 2350.0 MPa
- Markets
- Building & Construction
- Benefits
- Significantly reduced heat input
- Good transparency
- Excellent weather resistance
- Maximum impact strength
- Technology
- Plastics
- Available Sizes
Exolon® UV ClimateControl is available in thicknesses of 3 -12 mm and in the following colors. Colors :; Exolon®UV CC clear 2080; Exolon® UV CC green 2655
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
Excellent Transparency Properties; Good Environmental Stress Crack Resistance (ESCR); Good Impact Strength; Good UV Protection; Good Weather Stability; Long Shelf Life; Sunlight Resistant
- Plastics and Elastomers End Uses
- Glazing
- Roofing Elements
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength (23°C, 3 mm, Notched) | 80P | kg/m² | ISO 179-1eA |
| Charpy Impact Strength (23°C, Unnotched) | non-break | kg/m² | ISO 179-1eU |
| Flexural Modulus (2 mm/min) | 2350.0 | MPa | ISO 178 |
| Flexural Strength (2 mm/min) | 90.0 | MPa | ISO 178 |
| Izod Impact Strength (23°C, 3.2 mm, Notched) | 70P | kg/m² | ISO 180-A |
| Nominal Strain at Break (50 mm/min) | min. 50 | % | ISO 527-1,-2 |
| Tensile Modulus (1 mm/min) | 2350.0 | MPa | ISO 527-1,-2 |
| Yield Strain (50 mm/min) | 6.0 | % | ISO 527-1,-2 |
| Yield Stress (50 mm/min) | min. 60 | MPa | ISO 527-1,-2 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183-1 |
| Refractive Index (Procedure A) | 1.587 | — | ISO 489 |
| Water Absorption Equilibrium (23°C, 50% Relative Humidity) | 0.12 | % | ISO 62 |
| Water Absorption Saturation (23°C) | 0.3 | % | ISO 62 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 0.65 | 10⁻⁴/K | ISO 11359-1 |
| Temperature of Deflection Under Load (0.45 Mpa) | 140.0 | °C | ISO 75-1, -2 |
| Temperature of Deflection Under Load (1.80 Mpa) | 128.0 | °C | ISO 75-1, -2 |
| Thermal Conductivity (23°C) | 0.2 | W/mK | ISO 8302 |
| Vicat Softening Temperature (50 N, 50°C/h) | 148.0 | °C | ISO 306 |
Table 4 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Permanent Service Temperature (Without Load) | approx. 120 | °C |