To catalogue
Tuftec™ P1500
- CASE Ingredients Features
- Heat ResistanceImproved FlexibilityLow ViscosityThermal Resistance
- Chemical Family
- Styrenics
Asahi Kasei Tuftec™ P1500 is a selectively hydrogenated polymer. It is good as a base polymer for pressure sensitive adhesives (PSA). It has excellent compatibility with a variety of tackifiers. With blending tackifier and white oil, it provides solvent-borne as well as hot-melt adhesives. It is particularly suitable for hot-melt adhesive with low viscosity and good thermal stability.
Properties
- Physical Form
- Pellets
- Solid
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
Building & Construction — Building Materials
- Sealants & Caulks
Healthcare & Pharma — Medical
- Medical Tapes & Adhesives
Adhesives & Sealants — Medical Adhesives
- Other Medical Adhesives
Adhesives & Sealants — Packaging & Paper
- Tape & Label Adhesives
Printing & Packaging — Tapes, Labels & Adhesives
- Tapes & Labels
Product Families
CASE Ingredients — Resins & Binders
- Other Resins & Binders
Other characteristics
- Brand
- Tuftec
- End Uses
- Hot Melt Adhesive, Solventborne Adhesive
- Features
Heat Resistance, Improved Flexibility, Low Viscosity, Thermal Resistance
- Markets
- Adhesives & Sealants
- Building & Construction
- Healthcare & Pharma
- Printing & Packaging
- Regulations
- Regulation (EU) No 10/2011
- Technology
- CASE Ingredients
- Benefits and Features
Excellent compatibility with tackifiers; Available for hot melt adhesives for diaper and sanitary goods
- Adhesive & Sealant Type
- Hot Melt Adhesive
- Solventborne Adhesive
- Certifications and Compliance
- Regulation (EU) No. 10/2011 (PIM)
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.91 | g/cm3 | ISO 1183 |
| MFR at 190°C, 2.16kg Load | 4 | g/10 min | ISO 1133 |
| Viscosity as 15% solution in toluene | 35 | mPa s | ISO 7619 |
| Hardness Durometer Type A | 69 | Shore A | ISO 7619 |
| Tensile Strength Dumbbell: Type 1A 500 mm/min | 3.3 | MPa | ISO 37 |
| Elongation Dumbbell: Type 1A 500 mm/min | 780 | % | ISO 37 |
| 300% Tensile Stress | 2.1 | MPa | ISO 37 |
| Styrene | 30 | — | Asahi Kasei Method |
| Ethylene-Butylene Ratio | 70 | — | Asahi Kasei Method |