Nylon 6 A3130HR-25
- Chemical Family
- Polyamides
Nylon 6 A3130HR-25 is a Inorganic-fillered grade with low viscosity. It is used for injection molding applications.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Exterior & Body
- Interior
- Powertrain & UTH
Building & Construction — Building Materials
- Interior Fixtures
- Other Building Materials
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Nylon 6
- Polymer Name
- Polyamide 6 (PA 6)
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Plastics and Elastomers End Uses
- Appliances
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Construction Applications
- Consumer Applications
- Electrical Parts
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
33 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (Dry) | 5400 | Mpa | ISO 527-1 527-2 |
| Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 65 | kg/m² | ISO 179-1 |
| Charpy Impact Strength (Dry-as-Mold Condition) | 52 | kg/m² | ISO 179-1 |
| Tensile Modulus (Condition) | 2700 | Mpa | ISO 527-1 527-2 |
| Charpy Impact Strength (Conditioned) | 65 | kg/m² | ISO 179-1 |
| Tensile Strain at Break (Dry) | 3.5 | % | ISO 527-1 527-2 |
| Charpy Notched Impact Strength (Dry-as-Mold Condition) | 3 | kg/m² | ISO 179-1 |
| Tensile Strain at Break (Condition) | 4.8 | — | — |
| Charpy Impact Strength (Dry) | 52 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 5 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Conditioned) | 5 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Dry) | 3 | kg/m² | ISO 179-1 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 5 | 10⁻⁵/°C | ISO 11359-2 |
| Deflection Temperature (Under load 0.45MPa) | 195 | °C | ISO 75-2 |
| Deflection Temperature (Under load 1.8MPa) | 111 | °C | ISO 75-1 |
| Coefficient of Linear Thermal Expansion | 5 | 10⁻⁵/°C | ISO 11359-2 |
| Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 5 | 10⁻⁵/°C | ISO 11359-2 |
Table 3 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.6-1.0 | % | — |
| Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.6 - 1.0 | % | — |
| Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.6-1.0 | % | — |
| Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.6 - 1.0 | % | — |
| Water Absorption (23°C in Water 24H) | 1.4 | % | ISO 62 |
| Water Absorption (23°C, 50% RH Equilibirium) | 2.1 | % | ISO 62 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Flammability (mmt HB) | 0.75 | — | UL-94 |