Barstretch blown BRF 15
- Chemical Family
- PolyethylenesPolyolefins
Barbier Group Barstretch Blown BRF 15 is a high-performance blown stretch film that offers excellent performance and resistance to irregular, unstable and difficult to palletize load. This product is designed for all automatic machines with a pre-stretching of 250% to 300%.
Properties
- Physical Form
- Film
Product families
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Other characteristics
- Brand
- Barstretch
- Color
- Opaque, Translucent
- Opaque
- Translucent
- Features
- Good Adhesion, High Performance, Tacky
- Polymer Name
- Polyethylene Copolymer
- Size
- Standard thicknesses
- 15-17-20-22-30µm
- Standard lengths
- Adapted to a roll weight of 16 kg
- Markets
- Printing & Packaging
- Benefits
The belt effect limits parcels movement during transport and the adhesion between the multiple layers ensure perfect cohesion of the pallet.; This film has the tack on the outside with a high adhesion power and an inner slip face that eases the destocking of stacked pallets.; Coextruded stretch film.; 3 layers blown process.; Adhesion on the outside.; Specially designed for automatic wrapping of any load.
- PACKAGING
Stacking pallets 1000x1200x1200mm of 46 rolls, which are 736 kg, (indoor storage)
- Technology
- Plastics
- Packaging Type
- Rolls
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Good Adhesion
- High Performance
- Tacky
- Plastics and Elastomers End Uses
- Film
- Stretch Films
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Coextrusion
- Extrusion
- Film Extrusion
- Stretch Films Extrusion
Technical data
Table 1 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Average Thickness | 15.0 | µm | ISO 4592 |
| Tensile Strength at Yield (Elastic Limit, Machine Direction) | min. 13 | MPa | ISO 527-3 |
| Tensile Strength at Yield (Elastic Limit, Transverse Direction) | min. 8.7 | MPa | ASTM D882 |
| Tensile Strength at Break (Machine Direction) | min. 42 | MPa | ISO 527-3 |
| Tensile Strength at Break (Transverse Direction) | min. 25.3 | MPa | ASTM D882 |
| Elongation at Break (Machine Direction) | min. 480 | % | ISO 527-3 |
| Elongation at Break (Transverse Direction) | min. 600 | % | ASTM D882 |
| Dart Impact Test | min. 100 | g | ISO 7765/ASTM D1709 |
| Tearing Resistance (Machine Direction) | min. 70 | cN | ISO 6383/2 |
| Tearing Resistance (Transverse Direction) | min. 400 | cN | ASTM D1922 |
| Grade (Coextrusion of Polyethylene and Ethylene Copolymera) | 0.5 - 1.3 | g/10min | ISO 1133 |
| Density (Coextrusion of Polyethylene and Ethylene Copolymera) | 0.924 - 0.932 | g/10min | ISO 1183 |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Closed Width | -5 to 5 | mm | ISO 4592 |
| Nominale Thickness | -3 to 3 | % | ISO 4592 |
| Spot Thickness | -10 to 10 | % | ISO 4591 |
| Roll Edge | max. 3 | mm | ISO 4593 |
| Winding Variations | max. 2 | mm | ISO 4592 |