Barstretch M 15
- Chemical Family
- PolyethylenesPolyolefins
Barbier Group Barstretch M 15 offers exceptional performance and resistance to irregular pallets. Its flexibility makes it easy to use for everyone. Its transparency eases the identification of pallets in storage and its low noise when unwinding makes it comfortable in use.
Properties
- Physical Form
- Film
Product families
Printing & Packaging — Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Other characteristics
- Brand
- Barstretch
- Color
- Opaque, Translucent
- Opaque
- Translucent
- Features
- High Flexibility, High Performance
- Polymer Name
- Polyethylene Copolymer
- Size
- Standard thicknesses
- 15, 17, 20, 23 and 30µm
- Standard lengths
- 300 mm for 15 to 23µm and 450 and 200 m for 30 µm
- Markets
- Printing & Packaging
- Benefits
Coextruded stretch film.; 5 layers cast process.; Adhesion on the inside.; Specially designed for manual wrapping of any load.
- PACKAGING
Box of 6 rolls; Pallets 1000x1200x1200mm of 45 boxes, which are 270 rolls.
- Technology
- Plastics
- Packaging Type
- Boxes
- Rolls
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- High Flexibility
- High Performance
- Plastics and Elastomers End Uses
- Co-extruded Film
- Film
- Stretch Films
- Plastics and Elastomers Processing Methods
- Extrusion
- Stretch Films Extrusion
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Average Thickness | 15.0 | µm | ISO 4593 |
| Tensile Strength at Yield (Elastic Limit, Machine Direction) | 8.4 | MPa | ISO 527-3 |
| Tensile Strength at Yield (Elastic Limit, Transverse Direction) | 6.0 | MPa | ASTM D882 |
| Tensile Strength at Break (Machine Direction) | 35.0 | MPa | ISO 527-3 |
| Tensile Strength at Break (Transverse Direction) | 20.0 | MPa | ASTM D882 |
| Elongation at Break (Machine Direction) | 400.0 | % | ISO 527-3 |
| Elongation at Break (Transverse Direction) | 700.0 | % | ASTM D882 |
| Tearing Resistance (Machine Direction) | 40.0 | cN | ISO 7765 |
| Tearing Resistance (Transverse Direction) | 40.0 | cN | ASTM D1709 |
| Grade (Coextrusion of Polyethylene and Ethylene Copolymera) | 50.0 | g/10min | ISO 6383/2 |
| Density (Coextrusion of Polyethylene and Ethylene Copolymera) | 240.0 | g/10min | ASTM D1922 |