To catalogue
Torelina® A515
- Chemical Family
- Polyphenylene Sulfide (PPS)
Toray Torelina® A515 is a Polyphenylene Sulfide (PPS) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics includes flame rated and wear resistant.
Product families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- Torelina
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 12000.0 - 12000.0 MPa
- Additives Included
- Lubricant (Unspecified)
- Flame Rating
- IEC 60695-11-10 V0
- Technology
- Plastics
- Material Features
- Low Friction
- Tribological Modified
- Wear Resistant
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 145 | MPa | ASTM D 638 |
| Strain at break | 1.6 | % | ISO 527 |
| Flexural modulus, 23° | 12000 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 10 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 35 | kJ/m2 | ISO 179/1eU |
| Rockwell Hardness | 120 | Scale R | ASTM D 785 |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1680 | kg/m3 | ISO 1183 |
Table 3 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (normal) | 35 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 24 | E-6/K | ISO 11359-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 260 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 278 | °C | ISO 11357-1/-3 |
| Thickness tested | 0.7 | mm | — |
| Burning Behavior at thickness | V-0 | class | IEC 60695-11-10 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative permittivity (1MHz) | 3.4 | — | IEC 60250 |
| Dissipation factor (1MHz) | 20 | E-4 | IEC 60250 |