To catalogue
Toraycon® 1050M
- Chemical Family
- Polyesters
Product families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Toraycon
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Technology
- Plastics
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 55 | MPa | ASTM D638 |
| Elongation at Break | 12 | % | ASTM D 638 |
| Strain at break | 16 | % | ISO 527 |
| Flexural Strength | 81 | MPa | ASTM D 790 |
| Flexural modulus, 23° | 2500 | MPa | ISO 178 |
| Flexural Modulus | 2300 | MPa | ASTM D 790 |
| Charpy notched impact strength (+23°) | 3 | kJ/m2 | ISO 179/1eA |
| Izod Impact notched (1/8 in) | 34 | J/m | ASTM D 256 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (250°C/1 kg) | 47 | g/10 min | ASTM D 1238 |
| Melt Volume Flow Rate - MVR (250°C/2.16 kg) | 91 | cm3/10 min | ISO 1133 |
| Density | 1310 | kg/m3 | ISO 1183 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting temperature (10°C/min) | 224 | °C | ISO 11357-1/-3 |
| Melting Temperature | 224 | °C | ASTM D 3418 |
Table 4 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Intrinsic Viscosity | 0.74 | dl/g |