APCM DA 4517
- Chemical Family
- Epoxy & Epoxy Derivatives
APCM DA 4517 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 180°F (82°C) for three hour. Shorter cures times are available at higher temperatures. The system is designed to be post cured if the higher temperature service range is required.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Chassis & Brake
- Exterior & Body
- Interior
- Other Automotive Applications
- Powertrain & UTH
- Glazing & Window Elements
- Other Building Envelope & Roofing Applications
- Shingles & Tiles
- Fence Decks & Rails
- Interior Fixtures
- Other Building Materials
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
- Equipment & Parts
- Other Industrial Applications
- Tooling & Moldmaking
- Other Infrastructure Applications
- Pavement Highways Roads & Bridges
- Implants & Prosthetics
- Medical Devices & Assemblies
- Advanced Materials
- Body Armor
- Refining & Gas Processing
- Housings & Enclosures
- Other Parts & Components
- Printed Circuit Boards (PCBs)
- Other Power Water & Utilities Applications
- Power & Utilities
- Renewable Energy
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
- Thermoset Prepregs
Other characteristics
- End Uses
- Tanks
- Functions
- Prepreg
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Prepreg Processing, Vacuum Bagging
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Storage
Store material in a contaminate free container and store at O degrees F for extended storage. For shorter storage time requirements store at 40 degrees F, this enables quicker stabilization times.
- Cure Time Cycle
DA 4517 is designed to cure in one hour at 250°F (121°C), however this system may be cured at 180°F for three hours with post cures of elevated temperatures for one hour if higher temperature range applications are required. The prepreg may be cured using either standard heat-up methods or by in-hot, out-hot press applications. A pressure of 30 psi is recommended, however pressures of 10 to 50 psi may be used.
- Shelf LIfe
- 6 Months (40°F), 1 Year (0°F), 30 Days (75°F)
- Technology
- Composite Materials
- Composites End Use
- Tanks
- Composite Materials Functions
- Prepreg
- Composites Processing Methods
- Prepreg Processing
- Vacuum Bagging
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Volatiles | max. 1 | % |
| Tack | Medium | — |
| Form | Modified epoxy impregnated fabric | — |
| Resin Content | 45 to 50 | % by Weight |
| Separator | Release paper | — |
| Gel Time | 12 min. 36 sec. at 200°F | — |
| Gel Time (250°F) | 12 (36) | Minutes (Seconds) |
Table 2 of 2
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Tensile Strength at 75°F (24°C) | 72000 | psi |
| Tensile Strength at 180°F (82°C) | 69000 | psi |
| Tensile Modulus at 75°F (24°C) | 4.3 X 106 | psi |
| Tensile Modulus at 180°F (82°C) | 4.5 X 106 | psi |
| Flexural Strength at 75°F (24°C) | 114000 | psi |
| Flexural Strength at 180°F (82°C) | 118000 | psi |
| Flexural Strength at 350°F (177°C) | 42000 | psi |
| Flexural Strength after 24 hours at 350°F (177°C) | 42000 | psi |
| Flexural Modulus at 75°F (24°C) | 4.6 X 106 | psi |
| Flexural Modulus at 180°F (82°C) | 4.6 X 106 | psi |