POLIMAXX® 1111NXBA4
- Chemical Family
- PolyolefinsPolypropylenes (PP)
POLIMAXX®1111NXTA8 is a PP Homopolymer with 20% Barium Sulfate filler for injection molding process, featuring medium melt flow, high flexural modulus and high heat resistance. It is suitable for electrical appliances.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- POLIMAXX
- Polymer Name
- Polypropylene Compound (PP Compound)
- Melt Flow Index
- 12.0 - 12.0 g/10 min
- Fillers Included
- Barium Sulfate
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Technology
- Plastics
- Material Features
- High Flexural Modulus
- High Melt Flow
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- USA
- Processing Technique
Drying Temperature: 80-85⁰C, 2-3 hrs Processing Temperature: 190-240⁰C
- Plastics and Elastomers End Uses
- Appliances
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.06 | g/cm3 | D792 |
| Elongation At Break (23⁰C) | 30.0 | % | ASTM D638 |
| Flexural Modulus (23⁰C) | 2.0 | ×104kg/cm2 | ASTM D790 |
| Flexural Strength At Yield (23⁰C) | 440.0 | kg/cm2 | ASTM D790 |
| Heat Distortion Temperature (4.6 Kg/Cm2) | 120.0 | ⁰C | ASTM D648 |
| Izod Notched Impact ( 23⁰C) | 3.1 | Kg-cm/cm2 | ASTM D256 |
| Melt Flow Index (2.16 Kg/230⁰C) | 12.0 | g/10 min | ASTM D1238 |
| R °Ckwell Hardness ( 23⁰C) | 105.0 | R-Scale | ASTM D785 |
| Tensile Strength At Yield (23⁰C) | 345.0 | kg/cm2 | ASTM D638 |