POLIMAXX® U310T
- Chemical Family
- PolyethylenesPolyolefins
POLIMAXX®U310T is an Ultra High Molecular Weight Polyethylene in powder form with an average molecular weight about 3.7 Million g/mol. This resin has high abrasion resistance, low coefficient of friction properties and a high impact strength including transparent property. The resin is normally used for compression molding of sheet and special rod extrusion.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- POLIMAXX
- Polymer Name
Ultra High Molecular Weight Polyethylene (UHMWPE)
- Processing Methods
- Compression Molding
- Markets
- Industrial
- Technology
- Plastics
- Material Features
- Excellent UV Stability
- Good Abrasion Resistance
- High Impact Performance
- Low Friction
- Country Availability
- Canada
- China (Mainland)
- USA
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Average Molecular Weight (Cal.) | 3.7 x 106 | g/mol | Internal |
| Average Particle Size, X50 | 150.0 | μm | ASTM D1921 |
| Bulk Density | 0.4 | g/cm3 | ISO 60/ ASTM D1895 |
| Density | 0.93 | g/cm3 | ASTM D792 |
| Intrinsic Viscosity | 1765.0 | ml/g | ISO 1628 part 3 |
| Special Property (Haze) | max. 80 | % | — |
| Tensile Strength (Yield) | 18.0 | MPa | ISO527/ ASTM D638 |
| Viscosity Number (Vn) | 1970.0 | ml/g | ISO 1628 part 3 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 58.0 | Shore D | ISO868/ ASTM D2240 |
| Izod Impact Strength | NB | J/m | ASTM D256 |
| Melting Temperature (10 °C/Min) | 130 - 135 | °C | ASTM D3418 |
| Tensile Strength At Break | 30.0 | MPa | ISO527/ ASTM D638 |
| Ultimate Elonggation | min. 300 | % | ISO527/ ASTM D638 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point (1Kg) | 128.0 | °C | ISO 306/ASTM D1525 |