POLIMAXX® H611
- Chemical Family
- PolyethylenesPolyolefins
POLIMAXX®H611 is a High Molecular Weight Polyethylene with corrosion stabilizer (CS) in powder form with an average molecular weight about 0.6 Million g/mol. It's a suitable grade for general extrusion application. The high molecular weight yields several unique properties including high abrasion resistance, impact strength.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- POLIMAXX
- Polymer Name
- High Molecular Weight Polyethylene (HMWPE)
- Melt Flow Index
- 0.8 - 0.8 g/10 min
- Additives Included
- Stabilizer (Unspecified)
- Processing Methods
- Extrusion
- Markets
- Industrial
- Storage
IRPC High Molecular Weight Polyethylene shall be stored under dry condition with good ventilation system, protected from heat and direct sunlight. Store at temperature below 50 ◦C is strongly recommended.
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Corrosion Resistant
- High Impact Performance
- Country Availability
- Canada
- China (Mainland)
- USA
- Plastics and Elastomers End Uses
- Conveyor Parts
- Conveyors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Average Molecular Weight (Cal.) | 0.6 x 106 | g/mol | Margolies’s Equation |
| Average Particle Size, X50 | 125.0 | μm | Laser Scattering |
| Bulk Density | min. 0.40 | g/cm3 | ISO 60 |
| Density | 0.95 | g/cm3 | ISO 1183 |
| Intrinsic Viscosity | 520.0 | ml/g | ISO 1628 – 3 |
| Melt Flow Rate, Mfr (190 °C/21.6 Kg) | min. 0.8 | g/10 min | ISO 1133 |
| Special Property (Mfi 190°C/21.6 Kg) | 0.9 | g/10min | — |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 63.0 | Shore D | ISO 868 |
| Izod Impact Strength | NB | J/m | ASTM D256 |
| Tensile Strength (Break) | 35.0 | MPa | ISO527 |
| Tensile Strength (Yield) | 22.0 | MPa | ISO527 |
| Ultimate Elongation | min. 500 | % | ISO527 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature (10 °C/Min) | 130 - 138 | °C | ASTM D3418 |
| Vicat Softening Point (1Kg) | 125 - 128 | °C | ISO 306 |